Phosphorous pentoxide producing methods and phosphate ore feed agglomerates
View Patent ↗A phosphorous pentoxide producing method includes forming a reducing kiln bed using feed agglomerates containing a lignin sulfonate both inside the agglomerates and coating a surface of individual agglomerates. Freeboard particulates are generated from the agglomerates, an amount of particulates generated being less than would occur in the method with no lignin sulfonate. Kiln off gas is generated and phosphorous pentoxide is collected from the kiln off gas. The kiln discharges a residue containing processed agglomerates, less than 20% of the agglomerates' phosphate input to the kiln remaining in the residue. The percentage of input phosphate that remains in the residue is less than would occur in the method with no lignin sulfonate. The method may include forming green agglomerates. Controlling a drying rate of the green agglomerates may wick some of the lignin sulfonate onto the surface of individual drying agglomerates without adhering the agglomerates together.
1. A phosphorous pentoxide producing method comprising:
forming green feed agglomerates from a homogeneous blend of water, lignin sulfonate, phosphate ore particles, carbonaceous material particles, and silica particles, the green agglomerates containing about 0.1 to 4 wt % lignin sulfonate;
forming a reducing kiln bed using the feed agglomerates below an oxidizing freeboard of a counter-current rotary kiln, the bed having a length;
the agglomerates containing the phosphate ore particles, the carbonaceous material particles, sufficient silica particles for the agglomerates to exhibit a calcium plus magnesium-to-silica mole ratio of less than 1.0, and the lignin sulfonate both inside the agglomerates and coating a surface of individual agglomerates;
maintaining a bed temperature at or above 1180° C. along a portion of the bed length;
generating freeboard particulates from the agglomerates, an amount of particulates generated being less than would occur in the method with no lignin sulfonate; and
generating kiln off gas and collecting phosphorous pentoxide from the kiln off gas, the kiln discharging a residue containing processed agglomerates, less than 20% of the agglomerates' phosphate input to the kiln remaining in the residue, and the percentage of input phosphate that remains in the residue being less than would occur in the method with no lignin sulfonate.
2. The method of claim 1 wherein less than 10% of the agglomerates' phosphate input to the kiln remains in the residue and the calcium plus magnesium-to-silica mole ratio is less than 0.5.
3. The method of claim 1 further comprising controlling a drying rate of the green agglomerates and, as the water evaporates from the agglomerates, forming the lignin sulfonate coating on individual dried agglomerates by wicking some of the lignin sulfonate onto the surface of individual drying agglomerates without adhering the agglomerates together.
4. The method of claim 1 wherein the carbonaceous material particles comprise about 8 to 12 wt % volatiles and at least 80% of all particles exhibit a size less than 200 mesh.
5. A phosphorous pentoxide producing method comprising:
forming a reducing kiln bed using feed agglomerates below an oxidizing freeboard of a counter-current rotary kiln, the bed having a length;
the agglomerates containing phosphate ore particles, carbonaceous material particles, sufficient silica particles for the agglomerates to exhibit a calcium plus magnesium-to-silica mole ratio of less than 1.0, and a lignin sulfonate both inside the agglomerates and coating a surface of individual agglomerates, the lignin sulfonate coating having a thickness of about 1 to 50 micrometers and individual agglomerates containing a total of about 0.1 to 4 wt % lignin sulfonate including the coating;
maintaining a bed temperature at or above 1180° C. along a portion of the bed length;
generating freeboard particulates from the agglomerates, an amount of particulates generated being less than would occur in the method with no lignin sulfonate; and
generating kiln off gas and collecting phosphorous pentoxide from the kiln off gas, the kiln discharging a residue containing processed agglomerates, less than 20% of the agglomerates' phosphate input to the kiln remaining in the residue, and the percentage of input phosphate that remains in the residue being less than would occur in the method with no lignin sulfonate.
6. A phosphorous pentoxide producing method comprising:
forming a reducing kiln bed using feed agglomerates below an oxidizing freeboard of a counter-current rotary kiln, the bed having a length;
the agglomerates containing phosphate ore particles, carbonaceous material particles, sufficient silica particles for the agglomerates to exhibit a calcium plus magnesium-to-silica mole ratio of less than 1.0, and a lignin sulfonate both inside the agglomerates and coating a surface of individual agglomerates, the lignin sulfonate inside the agglomerates exhibiting a continuously decreasing concentration gradient of lignin sulfonate from the surface into individual agglomerates, individual agglomerates comprising a total of about 0.1 to 4 wt % lignin sulfonate including the coating;
maintaining a bed temperature at or above 1180° C. along a portion of the bed length;
generating freeboard particulates from the agglomerates, an amount of particulates generated being less than would occur in the method with no lignin sulfonate; and
generating kiln off gas and collecting phosphorous pentoxide from the kiln off gas, the kiln discharging a residue containing processed agglomerates, less than 20% of the agglomerates' phosphate input to the kiln remaining in the residue, and the percentage of input phosphate that remains in the residue being less than would occur in the method with no lignin sulfonate.
7. The method of claim 1 further comprising volatilizing at least a portion of the lignin sulfonate coating during bed heat up from about 650 to about 1180° C.
8. The method of claim 1 further comprising blanketing the bed with volatiles evolving at least partly from the lignin sulfonate during bed heat up from about 120 to about 650° C. and retaining a sacrificial layer of fixed carbon from the lignin sulfonate coating.
9. The method of claim 8 further comprising volatilizing at least a portion of the sacrificial layer during bed heat up from about 650 to about 1180° C.
10. A phosphorous pentoxide producing method comprising:
co-grinding a mixture containing phosphate ore, carbonaceous material, and silica;
homogeneously blending a lignin sulfonate with the co-ground mixture;
forming green feed agglomerates from the blended lignin sulfonate and co-ground mixture;
drying the green agglomerates and wicking some of the lignin sulfonate onto a surface of individual drying agglomerates, which forms a lignin sulfonate coating thereon, the dried agglomerates containing phosphate ore particles, carbonaceous material particles containing about 8 to 12 wt % volatiles, and sufficient silica particles for the dried agglomerates to exhibit a calcium plus magnesium-to-silica mole ratio of less than 0.5 and at least 80% of all particles exhibiting a size less than 200 mesh, the lignin sulfonate coating having a thickness of about 1 to 50 micrometers and a remainder of the lignin sulfonate exhibiting a continuously decreasing concentration gradient of lignin sulfonate from the surface into individual agglomerates, individual agglomerates comprising a total of about 0.1 to 4 wt % lignin sulfonate including the coating;
forming a reducing kiln bed using the dried agglomerates below an oxidizing freeboard of a counter-current rotary kiln, the bed having a length;
blanketing the bed with volatiles evolving at least partly from the lignin sulfonate during bed heat up from about 120 to about 650° C. and retaining a sacrificial layer of fixed carbon from the lignin sulfonate coating;
volatilizing at least a portion of the sacrificial layer during bed heat up from about 650 to about 1180° C.;
maintaining a bed temperature at or above 1180° C. along a portion of the bed length; and
generating kiln off gas and collecting phosphorous pentoxide from the kiln off gas, the kiln discharging a residue containing processed agglomerates, less than 10% of the agglomerates' phosphate input to the kiln remaining in the residue.
11. The method of claim 10 wherein the homogeneous blend of lignin sulfonate and the co-ground mixture further includes water and the drying comprises controlling a drying rate of the green agglomerates and, as the water evaporates from the agglomerates, forming the lignin sulfonate coating on individual dried agglomerates by wicking some of the lignin sulfonate onto the surface of individual drying agglomerates without adhering the agglomerates together.
12. The method of claim 10 wherein the green feed agglomerates comprise green feed balls exhibiting a greater than ¼ to less than ½ inch diameter prior to drying and the dried feed balls exhibit a dry crush strength greater than 25 pounds.
13. The method of claim 10 wherein the lignin sulfonate coating has a thickness of about 10 to 40 micrometers and the individual agglomerates comprise a total of about 0.4 to 2 wt % lignin sulfonate, including the coating.
14. The method of claim 10 further comprising generating freeboard particulates from the phosphate ore particles, an amount of particulates generated being less than would occur in the method with no lignin sulfonate.
15. The method of claim 10 wherein the percentage of input phosphate that remains in the residue is less than would occur in the method with no lignin sulfonate.
16. The method of claim 5 wherein less than 10% of the agglomerates' phosphate input to the kiln remains in the residue, the calcium plus magnesium-to-silica mole ratio is less than 0.5, and the carbonaceous material particles comprise about 8 to 12 wt % volatiles and at least 80% of all particles exhibit a size less than 200 mesh.
17. The method of claim 5 further comprising volatilizing at least a portion of the lignin sulfonate coating during bed heat up from about 650 to about 1180° C.
18. The method of claim 5 further comprising blanketing the bed with volatiles evolving at least partly from the lignin sulfonate during bed heat up from about 120 to about 650° C., retaining a sacrificial layer of fixed carbon from the lignin sulfonate coating, volatilizing at least a portion of the sacrificial layer during bed heat up from about 650 to about 1180° C.
19. The method of claim 6 wherein less than 10% of the agglomerates' phosphate input to the kiln remains in the residue, the calcium plus magnesium-to-silica mole ratio is less than 0.5, and the carbonaceous material particles comprise about 8 to 12 wt % volatiles and at least 80% of all particles exhibit a size less than 200 mesh.
20. The method of claim 6 further comprising volatilizing at least a portion of the lignin sulfonate coating during bed heat up from about 650 to about 1180° C.
21. The method of claim 6 further comprising blanketing the bed with volatiles evolving at least partly from the lignin sulfonate during bed heat up from about 120 to about 650° C., retaining a sacrificial layer of fixed carbon from the lignin sulfonate coating, volatilizing at least a portion of the sacrificial layer during bed heat up from about 650 to about 1180° C.