Plated steel sheet and method of hot-stamping plated steel sheet
View Patent ↗In a plated steel sheet having an aluminum-plating layer comprising at least Al formed on one side or both sides of the steel sheet, there is provided a plated steel sheet which, owing to the presence of a surface coating layer containing a compound having wurtzite crystal structure on the aluminum-plating layer, has excellent lubricity, prevents the plating thickness from becoming uneven during heating, and can improve formability and productivity in hot stamping, and a method of hot-stamping the plated steel sheet.
1. A method of hot-stamping a plated steel sheet comprising:
heating a blanked plated steel sheet comprising an aluminum-plating layer formed on one side or both sides of the steel sheet, and a surface coating layer containing ZnO overlaid on the aluminum-plating layer(s), and
forming the heated plated steel sheet by stamping,
wherein the surface coating layer contains at least a ZnO having a wurtzite crystal structure, and the ZnO content in the surface coating layer on each side of the steel sheet, calculated as Zn, is 0.5 to 7 g/m 2 ; and
wherein the aluminum-plating layer(s) contains 3 to 15 mass % of Si.
2. A method of hot stamping a plated steel sheet comprising:
box-annealing a coiled plated steel sheet comprising an aluminum-plating layer formed on one side or both sides of the steel sheet, and a surface coating layer containing ZnO overlaid on the aluminum-plating layer(s),
thereafter blanking and heating it, and stamping and forming the heated plated steel sheet,
wherein the surface coating layer contains at least a ZnO having a wurtzite crystal structure, and the ZnO content in the surface coating layer on each side of the steel sheet, calculated as Zn, is 0.5 to 7 g/m 2 ; and
wherein the aluminum-plating layer(s) contains 3 to 15 mass % of Si.
3. The method of hot-stamping a plated steel sheet according to claim 1 or 2 , wherein an average temperature-increase rate of heating by resistance heating or induction heating during heating prior to stamping is 50° C. to 300° C./sec from a plated steel sheet temperature of 600° C. to a temperature of 10° C. lower than a peak sheet temperature.