Nanocomposite particle and process of preparing the same
View Patent ↗A nanocomposite particle, its use as a catalyst, and a method of making it are disclosed. The nanocomposite particle comprises titanium dioxide nanoparticles, metal oxide nanoparticles, and a surface stabilizer. The metal oxide nanoparticles are formed hydrothermally in the presence of the titanium dioxide nanoparticles. The nanocomposite particle is an effective catalyst support, particularly for DeNO x catalyst applications.
1. A process for reducing nitrogen oxides in a waste stream by:
contacting the waste stream with a catalyst, wherein the catalyst includes:
(A) a nanocomposite particle, the nanocomposite particle comprising:
(i) predominantly anatase titanium dioxide nanoparticles;
(ii) metal oxide nanoparticles selected from the group consisting of zirconium dioxide, cerium dioxide, hafnium oxide, tin oxide, niobium oxide, tantalum oxide, and combinations thereof; and
(iii) a surface stabilizer selected from the group consisting of silicon dioxide, aluminum oxide, phosphorus pentoxide, aluminum silicate and aluminum phosphate, and combinations thereof; and
(B) at least one metal component comprising a metal selected from the group consisting of platinum, gold, silver, palladium, copper, tungsten, molybdenum, vanadium, iron, rhodium, nickel, manganese, chromium, cobalt, ruthenium, and combinations thereof.
2. The process of claim 1 , wherein the at least one metal component is selected from the group consisting of tungsten and vanadium.
3. The process of claim 2 , wherein the catalyst comprises about 0.1 to about 10 weight percent vanadium and about 4 to about 20 weight percent tungsten.
4. The process of claim 1 , wherein the metal oxide nanoparticles are zirconium dioxide.
5. The process of claim 1 , wherein the nanocomposite particles comprise about 50 to about 95 weight percent of titanium dioxide nanoparticles, about 2 to about 48 weight percent metal oxide nanoparticles, and about 2 to about 20 weight percent surface stabilizer.
6. The process of claim 1 , wherein the nanocomposite particle has a surface area greater than about 60 m 2 /g after being calcined at 800° C. for six hours.