Method for compression molding a dual core for a golf ball
View Patent ↗A method and system for compression molding a dual core of a golf ball is disclosed. The method may include a first cycle in which a top mold plate, a middle mold plate, and a bottom mold plate may be used to compression mold concave shells. During the first cycle, the top mold plate and the bottom mold plate may be held at a first temperature T 1 and the middle mold plate may be held at a second temperature T 2 . During the first cycle, the mold plates may be pressed together with a first pressure P 1 for a first time t 1 . A second cycle may include compression molding the concave shells about a solid core. During the second cycle, the top mold plate and the bottom mold plate may be held at the first temperature T 1 and pressed together with a second pressure P 2 for a second time t 2.
1. A method of making a golf ball core consisting of the following steps:
providing a compression molding apparatus having a top mold plate, middle mold plate, and a bottom mold plate;
placing a first core material comprising an uncured diene-containing composition between the top mold plate and the middle mold plate and placing a second core material comprising an uncured diene-containing composition between the middle mold plate and the bottom mold plate while maintaining both the top mold plate and the bottom mold plate at a first temperature T 1 and maintaining the middle mold plate at a second temperature T 2 that is lower than first temperature T 1 ;
in a first pressing step, pressing for a first time t 1 the first core material between the top mold plate and the middle mold plate to form at least one top concave shell and the second core material between the middle mold plate and the bottom mold plate to form at least one bottom concave shell, wherein T 1 , T 2 , and t 1 are selected such that the diene-containing composition of the at least one top concave shell and the diene-containing composition of the at least one bottom concave shell are partially cured;
removing the middle plate from between the top mold plate and the bottom mold plate;
placing a solid core between the at least one top concave shell and the at least one bottom concave shell; and
in a second pressing step, pressing for a second time t 2 the at least one top concave shell and the at least one bottom concave shell together between the top mold plate and the bottom mold plate while maintaining both the top mold plate and the bottom mold plate at the first temperature T 1 , wherein t 2 is selected such that the diene-containing composition of the at least one top concave shell and the diene-containing composition of the at least one bottom concave shell are cured together and
wherein t 2 is longer than t 1 .
2. The method according to claim 1 , wherein the second temperature T 2 is about 30° C. to about 70° C. lower than the first temperature T 1 .
3. The method according to claim 1 , wherein the first temperature T 1 ranges from about 125° C. to about 195° C.
4. The method according to claim 3 , wherein the first temperature T 1 ranges from about 140° C. to about 180° C.
5. The method according to claim 3 , wherein the second temperature T 2 ranges from about 70° C. to about 130° C.
6. The method according to claim 5 , wherein the second temperature T 2 ranges from about 85° C. to about 115° C.
7. The method according to claim 1 , wherein the solid core is formed of a thermoset material or a thermoplastic material.
8. A method of making a golf ball core according to claim 1 , wherein pressing in the first pressing step is carried out at-a first pressure P 1 of 85 kg/cm 2 to about 115 kg/cm 2 ; and-pressing in the second pressing step is carried out at a second pressure P 2 of 130 kg/cm 2 to about 170 kg/cm 2 .
9. The method according to claim 8 , wherein the first pressure P 1 ranges from about 95 kg/cm 2 to about 105 kg/cm 2 .
10. The method according to claim 8 , wherein the second pressure P 2 ranges from 145 kg/cm 2 to about 155 kg/cm 2 .
11. The method according to claim 1 , wherein the first time t 1 ranges from about 30 seconds to about 90 seconds.
12. The method according to claim 1 , wherein the second time t 2 ranges from about 400 seconds to about 550 seconds.