Hydrogenation of aromatics and other unsaturated organic compounds
View Patent ↗The present invention relates to supported Ni-catalysts optionally comprising Zn as a promoter, methods for the production of said catalysts and uses of said catalysts for the hydrogenation of a hydrocarbon feed.
1. A nickel (Ni)-catalyst comprising a support and Ni, wherein the size distribution of the Ni crystallites is bimodal with 30 to 70% of the Ni crystallites having an average size (diameter) in the range of from 1.0 to 2.5 nm and the remaining Ni crystallites having an average size (diameter) in the range of from 3.0 to 4.5 nm, and wherein the Ni is distributed in an outer shell region of the catalyst and a remaining centre of the catalyst in a concentration ratio in the range of from 3.0:1 to 1.3:1, the outer shell region of the catalyst having a penetration depth of 3 to 15% of the catalyst diameter.
2. The Ni-catalyst according to claim 1 having a pore volume of 0.4 to 0.5 ml/g and wherein the portion of the pore volume having pore radii of >5.0 nm is at least 75%.
3. The Ni-catalyst according to claim 1 , wherein the Ni content in the catalyst is 10 to 35 weight-%.
4. The Ni-catalyst according to claim 1 , wherein the Ni content in the catalyst is 10 to 24 weight-% and the concentration ratio of Ni of the outer shell region to the Ni of the centre is 2.5:1 to 1.3:1.
5. The Ni-catalyst according to claim 1 , wherein the Ni content in the catalyst is 24.1 to 35 weight-% and the concentration ratio of Ni of the outer shell region to the Ni of the centre is 3.0:1 to 1.5:1.
6. The Ni-catalyst according to claim 1 , wherein the centre of the catalyst has a diameter in the range of from 300 to 500 μm.
7. The Ni-catalyst according to claim 1 , wherein the specific Ni surface area is ≦135 m 2 /g Ni.
8. The Ni-catalyst according to claim 1 , wherein the support comprises Al 2 O 3 , Al 2 O 3 .SiO 2 or a mixture thereof.
9. The Ni-catalyst according to claim 1 , wherein the support is Al 2 O 3 having a surface area in the range of from 100 to 220 m 2 /g or Al 2 O 3 .SiO 2 having a surface area in the range of from 120 to 200 m 2 /g.
10. The Ni-catalyst according to claim 8 , wherein the support comprises Al 2 O 3 .SiO 2 and the SiO 2 content of the Al 2 O 3 .SiO 2 support is 2 to 8 weight-%.
11. The Ni-catalyst according to claim 1 , wherein up to 30% of the total Ni in the catalyst by weight is in the outer shell region.
12. A Ni-catalyst comprising a support and nickel wherein a centre of the catalyst comprises a base Ni concentration and a remaining outer shell region of the catalyst comprises an increased Ni concentration, the centre having a diameter of at least 200 μm and the outer shell region having a penetration depth in the range of from 40 μm to 200 μm, wherein the size distribution of the Ni crystallites of the catalyst is bimodal, with 30 to 70% of the Ni crystallites having an average size (diameter) in the range of from 1.0 to 2.5 nm and the remaining Ni crystallites having an average size (diameter) in the range of from 3.0 to 4.5 nm.
13. A Ni catalyst comprising a support and nickel, wherein the size distribution of the Ni crystallites of the catalyst is bimodal, with 30 to 70% of the Ni crystallites having an average size (diameter) in the range of from 1.0 to 2.5 nm and the remaining Ni crystallites having an average size (diameter) in the range of from 3.0 to 4.5 nm, wherein a centre of the catalyst comprises a base Ni concentration and a remaining outer shell region of the catalyst comprises an increased Ni concentration.
14. The Ni-catalyst according to claim 1 further comprising at least 1 weight-% zinc (Zn) as a promoter.