Positive electrode active material, and positive electrode and lithium secondary battery including the same
View Patent ↗Provided is a positive electrode active material. The positive electrode active material includes: a small-diameter active material having an average particle diameter of about 0.5 μm and a maximum particle diameter of less than about 1 μm; and a large-diameter active material having an average particle diameter of about 5 μm to about 20 μm and a maximum particle diameter of less than about 100 μm.
1. A positive electrode active material comprising:
a small-diameter active material having an average particle diameter of about 0.5 μm and a maximum particle diameter of less than about 1 μm; and
a large-diameter active material having an average particle diameter of about 5 μm to about 20 μm and a maximum particle diameter of less than about 100 μm,
wherein a weight ratio of the small-diameter active material and the large-diameter active material is 3+x:7−x (only when 0≦x≦6).
2. The positive electrode active material of claim 1 , wherein the small-diameter active material has an olivine structure of lithium metal phosphate (LiMPO 4 ).
3. The positive electrode active material of claim 1 , wherein the small-diameter active material is lithium iron phosphate (LiFePO 4 ).
4. The positive electrode active material of claim 2 , the small-diameter active material has an olivine structure of carbon-coated LiMPO 4 .
5. The positive electrode active material of claim 1 , wherein the weight ratio of the small-diameter active material and the large-diameter active material is 9:1.
6. The positive electrode active material of claim 1 , wherein the large-diameter active material comprises at least one selected from the group consisting of lithium manganese oxide, lithium cobalt oxide, lithium nickel oxide, lithium manganese cobalt oxide, lithium manganese nickel oxide, lithium cobalt nickel oxide, and lithium manganese cobalt nickel oxide.
7. A positive electrode comprising:
the positive electrode active material of claim 1 ;
a conductive material; and
a collector.
8. The positive electrode of claim 7 , wherein the collector has an uneven structure on a surface thereof.
9. The positive electrode of claim 8 , wherein the uneven structure is formed through etching.
10. The positive electrode of claim 9 , wherein an etched depth of the collector is less than or equal to ⅓ of a total thickness of the collector.
11. The positive electrode of claim 8 , wherein an average surface roughness (Ra) of the surface of the collector having the uneven structure is more than or equal to about 0.02 μm.
12. The positive electrode of claim 8 , wherein the collector has a capacity of less than or equal to about 120 μF/cm 3 .
13. The positive electrode of claim 8 , wherein the collector is formed of aluminum.
14. The positive electrode of claim 7 , wherein the conductive material is formed of carbon black or graphite particle.
15. The positive electrode of claim 7 , further comprising d) a binding material.
16. The positive electrode of claim 7 , wherein a thickness of the positive electrode is about 150 μm to about 170 μm.
17. A lithium secondary battery comprising the positive electrode of claim 7 .
18. The lithium secondary battery of claim 17 , wherein an output density of the lithium secondary battery is more than or equal to about 1000 W/Kg.
19. The positive electrode active material of claim 2 , wherein the small-diameter active material is lithium iron phosphate (LiFePO 4 ).