Recording medium for inkjet printing
View Patent ↗An inkjet recording medium and a coating composition for forming an inkjet recording medium. In accordance with one aspect of the present invention, an inkjet recording medium is disclosed comprising an inkjet-receptive coating on a paper substrate. The inkjet-receptive coating contains a synergistic combination of pigments, binder and a multivalent metal salt such that the inkjet recording medium exhibits improved inkjet print properties, particularly when printed with a high speed inkjet printer using pigmented inks.
1. An inkjet recording medium comprising:
a paper substrate; and
an inkjet-receptive coating comprising a primary pigment having a particle size distribution where at least 96% of the particles by weight have a particle size less than 2 microns;
a secondary pigment having an average particle size of 3 microns or less; the primary pigment comprises calcium carbonate;
a multivalent salt;
a dispersant selected from the group consisting of dispersants containing polyether polycarboxylate salts, dispersants containing polyoxyalkylene salts and combinations thereof; and
a binder wherein said binder is present in an amount from about 2 to 15 parts by weight of based on 100 parts total pigments.
2. The inkjet recording medium of claim 1 wherein the binder comprises a biopolymer.
3. The inkjet recording medium of claim 1 wherein the binder is a calcium stable vinyl acetate or styrene butadiene latex.
4. The inkjet recording medium of claim 3 wherein said binder comprises biopolymer particles.
5. The inkjet recording medium of claim 4 wherein said binder comprises starch nanoparticles.
6. The inkjet recording medium of claim 5 wherein said nanoparticles have an average particle size of less than 400 nm.
7. The inkjet recording medium of claim 6 wherein said binder comprises a biopolymer latex conjugate comprising a biopolymer-additive complex reacted with a crosslinking agent.
8. The inkjet recording medium of claim 1 wherein said coating comprises a retention aid present in an amount of about 0.1 to 1 part per 100 parts of total pigments.
9. The inkjet recording medium of claim 1 wherein the primary pigment comprises aragonite.
10. The inkjet recording medium of claim 1 further comprising at least one secondary pigment selected from the group consisting of calcium carbonate and plastic pigments.
11. The inkjet recording medium of claim 1 wherein said medium has a density to mottle value of at least 1.5 when printed with a pigmented inkjet ink.
12. The inkjet recording medium of claim 1 wherein said coating further comprises a co-binder selected from the group consisting of protein binders, polyvinyl alcohol, starch and mixtures thereof.
13. The inkjet recording medium of claim 1 wherein said primary pigment is present in an amount of about 35 to 85 parts based on 100 parts total pigments.
14. The inkjet recording medium of claim 1 wherein said coating further comprises a plastic pigment present in an amount of about 2 to 12 parts per 100 parts total pigments.
15. The inkjet recording medium of claim 1 wherein said coating is present at a coat weight of about 2 to 8 lbs./ream (3,300 ft. 2 ).
16. The inkjet recording medium of claim 1 wherein the multivalent metal salt is selected from the group consisting of calcium chloride, calcium acetate, calcium nitrate, magnesium chloride, magnesium acetate, magnesium nitrate, magnesium sulfate, barium chloride, barium nitrate, zinc chloride, zinc nitrate, aluminum chloride, aluminum hydroxychloride, aluminum nitrate and mixtures thereof.
17. The inkjet recording medium of claim 16 wherein the multivalent metal salt comprises calcium chloride.
18. The inkjet recording medium of claim 1 wherein said binder comprises starch.
19. An inkjet recording medium comprising:
a paper substrate; and
an inkjet-receptive coating comprising a primary pigment having a particle size distribution where at least 96% of the particles by weight have a particle size less than 2 microns, the primary pigment comprising aragonite;
a cationic secondary pigment having an average particle size of 3 microns or less;
calcium chloride;
a dispersant selected from the group consisting of dispersants containing polyether polycarboxylate salts, dispersants containing polyoxyalkylene salts and combinations thereof; and
a binder wherein said binder is present in an amount from about 2 to 15 parts by weight of based on 100 parts total pigments.