Golf ball composition
This invention pertains to a golf ball which includes a core, optionally one or more intermediate layers; and an outer cover layer. The outer cover layer and/or one or more intermediate layers includes a blend of a) 2 to 60 wt % (based on the total weight of the blend composition) of a cyclic olefin polymer which includes a norbornene-based monomer having the general formula; where R 18 to R 21 independently represent a hydrogen atom, a halogen atom or a hydrocarbon group and m is from 0 to about 3; and b) about 40 to about 98 wt % (based on the total weight of the blend composition) of one or more additional polymer components. The blend composition has a melt flow index (MFI) from 1 to 80 g/10 min., a material hardness of 30 to 90 Shore D, and a flex modulus of 10 to 120 kpsi.
1. A golf ball comprising;
I a core;
II optionally one or more intermediate layers; and
III an outer cover layer, and
wherein said outer cover layer comprises a blend composition comprising;
A from about 2 to about 60 wt % (based on the total weight of the blend composition) of a cyclic olefin polymer comprising a norbomene-based monomer having the general formula;
wherein R 18 to R 21 independently represent a hydrogen atom, a halogen atom or a hydrocarbon group and m is from 0 to about 3; and
B from about 40 to about 98 wt % (based on the total weight of the blend composition) of one or more additional polymer components selected from the group consisting of a block copolymer, a polyalkenamer, a thermoplastic or thermoset polyurethane or thermoplastic or thermoset polyurea, and any and all combinations thereof; and
wherein said blend composition has;
i a melt flow index (MFI) of from about 1 to about 80 g/10 min.;
ii a material hardness of from about 30 to about 90 Shore D; and
iii a flex modulus of from about 10 to about 120 kpsi.
2. The golf ball of claim 1 wherein said blend composition comprises;
A from about 8 to about 35 wt % (based on the total weight of the blend composition) of said cyclic olefin copolymer wherein
a in said norbornene-based monomer, R 18 to R 21 are selected from the group consisting of hydrogen atoms, halogen atoms, C 1 -C 20 alkyl, C 3 -C 20 cycloalkyl group, and C 6 -C 20 aromatic hydrocarbon groups and any and all combinations thereof; and m is 0 to 1; and
b said cyclic olefin copolymer further comprises a monomer selected from the group consisting of ethylene, propylene, 1-butene, 1-pentene, 3-methyl-1-butene, 1-hexene, 3-methyl-1-pentene, 4-methyl-1-pentene, 1-heptene, 1-octene, vinylcyclohexane, 1-nonene, 3-cyclohexyl-1-propene, 1-decene, 1-undecene and 1-dodecene, styrene, α-methylstyrene, p-methylstyrene, p-chlorostyrene and indene 1,3-butadiene and isoprene and any and all combinations thereof;
B from about 65 to about 92 wt % (based on the total weight of the blend composition) of said additional blend component which is selected from the group consisting of a block copolymer, a polyalkenamer, a thermoplastic or thermoset polyurethane or thermoplastic or thermoset polyurea, and any and all combinations thereof; and
wherein said blend composition has;
i a melt flow index (MFI) of from about 8 to about 40 g/10 min.;
ii a material hardness of from about 40 to about 75 Shore D; and
iii a flex modulus of from about 40 to about 90 kpsi.
3. The golf ball of claim 1 wherein said blend composition comprises;
A from about 10 to about 25 wt % (based on the total weight of the blend composition) of said cyclic olefin copolymer comprising;
a said norbornene-based monomer component wherein to R 18 to R 21 are hydrogen and m is 0 to 1; and
b a monomer selected from the group consisting of ethylene, propylene, 1-butene, styrene, 1,3-butadiene and isoprene and any and all combinations thereof;
B from about 75 to about 90 wt % (based on the total weight of the blend composition) of said additional blend component which is selected from the group consisting of a block copolymer, a polyalkenamer a thermoplastic polyurethane, a thermoplastic polyurea, a thermoset polyurethane, a thermoset polyurea, and any and all combinations thereof; and
wherein said blend composition has;
i a melt flow index (MFI) of from about 10 to about 30 g/10 min.;
ii a material hardness of from about 45 to about 70 Shore D; and
iii a flex modulus of from about 50 to about 80 kpsi.
4. The golf ball of claim 1 wherein said core;
a has a diameter of from about 0.5 to about 1.62 inches;
b has a PGA compression of less than about 100; and
c comprises a peptizer selected from the group consisting of an organic sulfur compound, a metal salt of an organic sulfur compound, a non-metal salt of an organic sulfur compound, and any and all combinations thereof.
5. The golf ball of claim 1 wherein said core;
a has a diameter of from about 0.7 to about 1.60 in; and
b has a PGA compression of less than about 90.
6. The golf ball of claim 5 wherein the hardness of the core increases progressively outwards from the center.
7. The golf ball of claim 5 wherein the hardness of the core decreases progressively outwards from the center.