Polyamide resin composition

1. A polyamide resin composition for a reflector comprising:

(A) crystalline polyamide resin having a glass transition temperature (Tg) of about 50 to about 100° C.;

(B) crystalline polyamide resin having a glass transition temperature (Tg) of about 110 to about 160° C.;

(C) inorganic filler;

(D) white pigment; and

(E) light stabilizer;

wherein a molded article formed of the polyamide resin composition has a 60° surface gloss of more than about 85% and a surface reflectance of about 70 to about 100% at a 440 nm wavelength light measured after the molded article is illuminated by a LED light source having a wavelength of 460 nm for 120 hours in a constant temperature and humidity environment of 85° C. and 85% relative humidity.

2. The polyamide resin composition for a reflector of claim 1 , wherein the molded article formed of the polyamide resin composition has a yellow index of less than about 10, measured after illuminated of the molded article by a LED light source having a wavelength of 460 nm for 120 hours in a constant temperature and humidity environment of 85° C. and 85% relative humidity.

3. The polyamide resin composition for a reflector of claim 1 , wherein the crystalline polyamide resin (B) has a glass transition temperature (Tg) of about 120 to about 160° C.

4. The polyamide resin composition for a reflector of claim 1 , wherein the inorganic filler (C) comprises a glass fiber having an average length of about 0.1 to about 20 mm and an aspect ratio of about 10 to about 2,000.

5. The polyamide resin composition for a reflector of claim 1 , wherein the white pigment (D) comprises titanium oxide, zinc sulfide, white lead, zinc sulfate, aluminum oxide or a combination thereof.

6. The polyamide resin composition for a reflector of claim 1 , wherein the light stabilizer (E) comprises a hindered amine-based compound.

7. The polyamide resin composition for a reflector of claim 1 comprising;

(A) about 10 to about 70% by weight of the crystalline polyamide resin having a glass transition temperature (Tg) of about 50 to about 100° C.;

(B) about 10 to about 70% by weight of the crystalline polyamide resin (B) having a glass transition temperature (Tg) of about 110 to about 160° C.;

(C) about 10 to about 60% by weight of the inorganic filler;

(D) about 10 to about 50% by weight of the white pigment, and

(E) about 0.05 to about 2 parts by weight of the light stabilizer, based on about 100 parts by weight of the crystalline polyamide resin (A), the crystalline polyamide resin (B), the inorganic filler (C) and the white pigment (D).

8. A molded article prepared from the polyamide resin composition for a reflector of claim 1 .

9. The polyamide resin composition for a reflector of claim 7 , comprising:

(A) about 20 to about 40% by weight of the crystalline polyamide resin having a glass transition temperature (Tg) of about 50 to about 100° C.; and

(B) about 20 to about 40% by weight of the crystalline polyamide resin having a glass transition temperature (Tg) of about 110 to about 160° C.

10. The polyamide resin composition for a reflector of claim 1 , wherein the crystalline polyamide resin (A) has a glass transition temperature (Tg) of 90 to about 100° C.

11. The polyamide resin composition for a reflector of claim 10 , wherein the crystalline polyamide resin (B) has a glass transition temperature (Tg) of 138 to about 160° C.

12. The polyamide resin composition for a reflector of claim 11 , comprising:

about 20 to about 40% by weight of the crystalline polyamide resin (A); and

about 20 to about 40% by weight of the crystalline polyamide resin (B).