View Patent ↗A graphite film having excellent thermal conductivity, surface hardness, surface adhesion and appearance can be obtained. Further, a thick graphite film in which each of such properties is excellent can be obtained. There is provided a process for producing a graphite film in which a polymer film is thermally treated at a temperature of 2,000° C. or more, the process comprising the step of bringing a polymer film into contact with a substance containing a metal during graphitization treatment. When a polymer film having a high plane orientation is used as a raw material and the raw material is brought into contact with a metal to thermally treat the material, a problem of separation of graphite from the surface can be solved which has not been solved by the prior art, and furthermore a graphite can be obtained having excellent thermal conductivity, surface hardness, density and surface adhesion.
1. A process for producing a graphite film in which a polymer film is thermally treated at a temperature of 2,000° C. or more, the process comprising the step of employing a container containing a metal to bring a polymer film into contact with a substance containing a metal during thermal treatment, wherein
The container containing the metal is a graphite container composed of graphite containing the metal, or a container in which a graphite plate composed of graphite containing the metal is placed.
2. The process for producing a graphite film according to claim 1 , wherein the container can be closed.
3. The process for producing a graphite film according to claim 1 or claim 2 , wherein the metal is one or more selected from the group consisting of elements of Groups 4, 5, 6, 7, 8, 9, 10, 11, 12 and 13 according to the IUPAC (International Union of Pure and Applied Chemistry) Nomenclature of Inorganic Chemistry, revised edition (1989), lithium, beryllium, sodium, magnesium, potassium, calcium, barium, silicon, germanium, selenium, tin, lead and bismuth.
4. The process for producing a graphite film according to claim 1 or claim 2 , wherein the metal is one or more selected from the group consisting of titanium, vanadium, chromium, manganese, iron, cobalt, nickel, copper, zinc, zirconium, niobium, molybdenum, technetium, ruthenium, rhodium, palladium, silver, cadmium, hafnium, tantalum, tungsten, rhenium, osmium, iridium, platinum, gold and mercury.
5. The process for producing a graphite film according to claim 1 or claim 2 , wherein the polymer film is composed of one or more polymers selected from the group consisting of polyimide, polyamide, polyoxadiazole, polybenzoxazole, polybenzobisoxazole, polythiazole, polybenzothiazole, polybenzobisthiazole, poly(p-phenylene vinylene), polybenzimidazole and polybenzobisimidazole.
6. The process for producing a graphite film according to claim 5 , wherein the polymer film is a polyimide film having a birefringence of 0.08 or more.
7. The process for producing a graphite film according to claim 5 , wherein the polymer film is a polyimide film having a birefringence of 0.12 or more.
8. The process for producing a graphite film according to claim 5 , wherein the polyimide film can be prepared by imidizing a polyamide acid as a precursor using a dehydrating agent and an imidization promoter.
9. The process for producing a graphite film according to claim 5 , wherein the polyimide film can be prepared by imidizing a polyamide acid containing pyromellitic acid dianhydride and p-phenylenediamine using a dehydrating agent and an imidization promoter.
10. The process for producing a graphite film according to claim 5 , wherein the polyimide film can be prepared by synthesizing a prepolymer having an acid dianhydride at each terminal from a diamine and the acid dianhydride; synthesizing a polyamide acid by reaction of the prepolymer with a diamine differing from the diamine; and imidizing the polyamide acid.
11. The process for producing a graphite film according to claim 5 , wherein the polymer film contains the metal.
12. A graphite film having a thermal diffusivity of 7×10 −4 m 2 /s or more and a pencil hardness of 2B or harder.
13. A graphite film having a thermal diffusivity of 7×10 −4 m 2 /s or more and a pencil hardness of 2B or harder, which can be produced by the process according to claim 1 or claim 2 .
14. The graphite film according to claim 12 , which has a thickness of 50 μm or more.
15. The process for producing a graphite film according to claim 1 , wherein the graphite film has a pencil hardness of 2B or harder.
16. The process for producing a graphite film according to claim 1 , wherein the graphite film has a thermal diffusivity of 7×10 −4 m 2 /s or more and a pencil hardness of 2B or harder.