Asphalt paving materials and methods for making the same
View Patent ↗An asphalt paving material comprises an asphalt binder present in an amount of from about 3 to about 8 weight percent of the asphalt paving material. The asphalt binder comprises base asphalt and oxidized polyolefin that is present in an amount of from about 0.25 to about 10 weight percent of the base asphalt. Aggregate is present in an amount of about 92 to about 97 weight percent of the asphalt paving material. The oxidized polyolefin effectively adheres the asphalt binder to the aggregate so as to resist stripping of the asphalt binder from the aggregate caused by moisture.
1. An asphalt paving material comprising:
an asphalt binder present in an amount of from about 3 to about 8 wt. % of the asphalt paving material, the asphalt binder comprising base asphalt and a polymer, wherein the polymer consists of oxidized high density polyethylene homopolymer and is present in an amount of from about 0.25 to about 10 wt. % of the base asphalt; and
aggregate present in an amount of from about 92 to about 97 wt. % of the asphalt paving material, wherein the polymer effectively adheres the asphalt binder to the aggregate so as to resist stripping of the asphalt binder from the aggregate caused by moisture.
2. The asphalt paving material according to claim 1 , wherein the polymer effectively adheres the asphalt binder to the aggregate such that the asphalt paving material has an AASHTO T-283 tensile strength ratio of at least about 0.65.
3. The asphalt paving material according to claim 1 , wherein the polymer effectively adheres the asphalt binder to the aggregate such that the asphalt paving material has an AASHTO T-283 tensile strength ratio of at least about 0.75.
4. The asphalt paving material according to claim 1 , wherein the polymer is present in an amount of from about 1 to about 4 wt. % of the base asphalt.
5. The asphalt paving material according to claim 1 , wherein the polymer has an acid number of from about 5 to about 50.
6. The asphalt paving material according to claim 1 , wherein the asphalt binder comprises substantially no anti-stripping agent.
7. A method for preparing an asphalt paving material, the method comprising the step of mixing asphalt binder and aggregate at conditions effective to form the asphalt paving material, wherein the asphalt binder is present in an amount of from about 3 to about 8 wt. % of the asphalt paving material and the aggregate is present in an amount of from about 92 to about 97 wt. % of the asphalt paving material, the asphalt binder comprises base asphalt and a polymer wherein the polymer consists of oxidized high density polyethylene homopolymer and is present in an amount of from about 0.25 to about 10 wt. % of the base asphalt, and wherein the polymer effectively adheres the asphalt binder to the aggregate so as to resist stripping of the asphalt binder from the aggregate caused by moisture.
8. The method according to claim 7 , wherein the step of mixing the asphalt binder and the aggregate includes mixing the asphalt binder and the aggregate at a temperature of from about 120 to about 190° C.
9. The method according to claim 7 , further comprising the step of combining the base asphalt and the polymer to form the asphalt binder prior to the step of mixing the asphalt binder and the aggregate.
10. The method according to claim 7 , further comprising the step of combining the polymer and the aggregate at conditions effective to coat the aggregate with the polymer prior to the step of mixing the asphalt binder and the aggregate, and the step of mixing the asphalt binder and the aggregate includes adding the base asphalt to the aggregate that is coated with the polymer.
11. The method according to claim 10 , wherein the step of combining the polymer and the aggregate includes combining the polymer and the aggregate at a temperature of from about 120 to about 190° C.
12. The method according to claim 7 , wherein the step of mixing the asphalt binder and the aggregate includes mixing the aggregate and the asphalt binder that comprises substantially no anti-stripping agent.