Method of manufacturing heavy-wall seamless steel pipe
View Patent ↗A steel pipe with a wall thickness over 30 mm is subjected to heat treatment of quenching and tempering using a temperature range of at least not less than 750° C. during the heating stage, makes it possible to obtain a heavy-wall seamless steel pipe having excellent toughness by resulting grain refinement. Quenching is by performing water cooling after heating the steel pipe to a temperature in the range of not less than 900° C. to not more than 1000° C. by using, as a heating means, induction heating at a frequency of not more than 200 Hz. Tempering is performed at a temperature in the range of not less than 500° C. to not more than 750° C. Preferably, after the heating by induction heating, a soaking treatment is performed in the temperature range of not less than 900° C. to not more than 1000° C. for 10 minutes or less followed by water cooling.
1. A method of manufacturing a heavy-wall seamless steel pipe comprising subjecting a steel pipe with a wall thickness over 30 mm to a quench-and-tempering treatment process comprising a quenching step (a) and a tempering step (b) as below, in the order as described, the pipe being made through a pipe making step by hot working:
(a) a quenching step that involves heating the steel pipe from room temperature to a temperature in the range of not less than 600° C. to nor more than 750° C. by using an atmosphere temperature control heating furnace, thereafter heating the steel pipe to a temperature in the range of not less than 900° C. to not more than 1000° C. by using induction heating at a frequency of not more than 60 Hz in a temperature range of at least not less than 750° C. during the heating stage, and subsequently performing quenching by water cooling; and
(b) a tempering step that involves performing tempering at a temperature in the range of not less than 500° C. to not more than 750° C.
2. The method of manufacturing a heavy-wall seamless steel pipe according to claim 1 , wherein the quenching step further involves a soaking treatment in a temperature range of not less than 900° C. to not more than 1000° C. for 10 minutes or less between the induction heating and the quenching.
3. The method of manufacturing a heavy-wall seamless steel pipe according to claim 2 , wherein the soaking treatment is performed in an atmosphere temperature control heating furnace.
4. The method of manufacturing a heavy-wall seamless steel pipe according to claim 1 , wherein the seamless steel pipe to be subjected to the quench-and-tempering treatment process is water cooled from a temperature of not less than Ar 3 point after pipe making by hot working.
5. The method of manufacturing a heavy-wall seamless steel pipe according to claim 2 , wherein the seamless steel pipe to be subjected to the quench-and-tempering treatment process is water cooled from a temperature of not less than Ar 3 point after pipe making by hot working.
6. The method of manufacturing a heavy-wall seamless steel pipe according to claim 1 , wherein the seamless steel pipe to be subjected to the quench-and-tempering treatment process is soaked at a temperature in the range of not less than 900° C. to not more than 1000° C. and is subsequently water cooled after pipe making by hot working.
7. The method of manufacturing a heavy-wall seamless steel pipe according to claim 2 , wherein the seamless steel pipe to be subjected to the quench-and-tempering treatment process is soaked at a temperature in the range of not less than 900° C. to not more than 1000° C. and is subsequently water cooled after pipe making by hot working.
8. The method of manufacturing a heavy-wall seamless steel pipe according to claim 1 , wherein the quench-and-tempering treatment involves an additional quenching step as set forth in claim 1 between the quenching step as set forth in claim 1 and the tempering step.
9. The method of manufacturing a heavy-wall seamless steel pipe according to claim 2 , wherein the quench-and-tempering treatment involves the additional quenching step according to step (a) between the quenching step further involving soaking and the tempering step.
10. The method of manufacturing a heavy-wall seamless steel pipe according to claim 2 , wherein the quench-and-tempering treatment involves the additional quenching step involving soaking between the quenching step involving soaking and the tempering step.
11. The method of manufacturing a heavy-wall seamless steel pipe according to claim 3 , wherein the quench-and-tempering treatment involves the additional quenching step involving soaking between the quenching step involving soaking in the atmosphere temperature control heating furnace and the tempering step.
12. The method of manufacturing a heavy-wall seamless steel pipe according to claim 4 , wherein the quench-and-tempering treatment involves an additional quenching step according to step (a) between the quenching step involving water cooling and the tempering step.
13. The method of manufacturing a heavy-wall seamless steel pipe according to claim 5 , wherein the quench-and-tempering treatment involves an additional quenching step according to step (a) between the quenching step involving water cooling and the tempering step.
14. The method of manufacturing a heavy-wall seamless steel pipe according to claim 6 , wherein the quench-and-tempering treatment involves an additional quenching step according to step (a) between the quenching step involving water cooling and the tempering step.
15. The method of manufacturing a heavy-wall seamless steel pipe according to claim 6 , wherein the quench-and-tempering treatment involves the additional quenching step involving soaking between the quenching step involving water cooling and the tempering step.
16. The method of manufacturing a heavy-wall seamless steel pipe according to claim 1 , wherein in performing the induction heating, the seamless steel pipe is induction heated without being transferred in a longitudinal direction during heating by using an induction heating device having a coil length longer than the length of the steel pipe to be induction heated.
17. The method of manufacturing a heavy-wall seamless steel pipe according to claim 2 , wherein in performing the induction heating, the seamless steel pipe is induction heated without being transferred in a longitudinal direction during heating by using an induction heating device having a coil length longer than the length of the steel pipe to be induction heated.