β-type titanium alloy
View Patent ↗The present invention provides a β-type titanium alloy that includes, by mass %, when Al: 2 to 5%, 1) Fe: 2 to 4%, Cr: 6.2 to 11%, and V: 4 to 10%, 2) Fe: 2 to 4%, Cr: 5 to 11%, and Mo: 4 to 10%, or 3) Fe: 2 to 4%, Cr: 5.5 to 11%, and Mo+V (total of Mo and V): 4 to 10% in range, and a balance of substantially Ti. These include Zr added in amounts of 1 to 4 mass %. Furthermore, by making the oxygen equivalent Q 0.15 to 0.30 or leaving the alloy in the work hardened state or by applying both, the tensile strength before aging heat treatment can be further increased.
1. A β-type titanium alloy, which will consist of an α phase and a β phase after aging, containing, by mass %, Al: 2 to 5%, Fe: 2.6 to 4%, Cr: 6.2 to 9%, and V: 4 to 10% in ranges and having a balance of Ti and unavoidable impurities,
wherein:
when a Vicker's hardness is randomly measured at six points in each of three L-cross-sections, a difference between a maximum value and a minimum value thereof is in a range from 10 to 20,
a tensile strength of the β-type titanium alloy before aging is 920 MPa or more, and
the β-type titanium alloy does not contain Sn,
the α phase is substantially uniformly precipitated after solution treatment, drawing and aging.
2. The β-type titanium alloy as set forth in claim 1 characterized in that an oxygen equivalent Q of formula [1] is 0.15 to 0.30:
Oxygen equivalent Q=[O]+2.77[N] formula [1]
where, [O] is O (oxygen) content (mass %) and [N] is N content (mass %).
3. A worked product obtained by work hardening the β-type titanium alloy as set forth in claim 1 .
4. A β-type titanium alloy, which will consist of an α phase and a p phase after aging, containing, by mass %, Al: 2 to 5%, Fe: 2.6 to 4%, Cr: 5.5 to 9%, and Mo+V (total of Mo and V): 4 to 10% by Mo: 0.5% or more and V: 0.5% or more in ranges and having a balance of Ti and unavoidable impurities,
wherein:
when a Vicker's hardness is randomly measured at six points in each of three L-cross-sections, a difference between a maximum value and a minimum value thereof is in a range from 10 to 20,
a tensile strength of the β-type titanium alloy before aging is 920 MPa or more, and
the β-type titanium alloy does not contain Sn,
the α phase is substantially uniformly precipitated after solution treatment drawing and aging.