Resin composition, multilayer structure using same and method for producing same
View Patent ↗Disclosed is a resin composition comprising (A) a saponified ethylene-vinyl ester copolymer and (B) a completely or partially dehydrated polyvalent metal sulfate hydrate. Preferably, the component (B) is a completely or partially dehydrated 2-valent metal sulfate hydrate. The resin composition can suppress increasing viscosity in preparation thereof as well as production of the multilayer structure therefrom. A molded article can be stably produced and recover quickly gas barrier property deteriorated by hot water treatment and additionally maintain the superior gas barrier property.
1. A resin composition comprising (A) a saponified ethylene-vinyl ester copolymer, (B) a completely dehydrated magnesium sulfate, and a polyamide resin,
wherein the content ratio (B/A) of component (B) to component (A) is in the range of 50/50 to 1/99 in terms of weight ratio, and
wherein the amount of the polyamide resin is 1 to 30% by weight based on the weight of component (A).
2. The resin composition according to claim 1 , wherein the polyamide resin is a terminal-modified polyamide resin.
3. The resin composition according to claim 1 , further comprising a plate inorganic filler.
4. A multilayer structure comprising at least one layer of a resin composition comprising (A) a saponified ethylene-vinyl ester copolymer, (B) a completely dehydrated magnesium sulfate, and a polyamide resin,
wherein the content ratio (B/A) of component (B) to component (A) is in the range of 50/50 to 1/99 in terms of weight ratio, and
wherein the content of the polyamide resin is 1 to 30% by weight based on the weight of component (A).
5. A multilayer structure according to claim 4 , further comprising layers containing a hydrophobic thermoplastic resin, the said layers being provided on both sides of the layer of the resin composition.
6. The multilayer structure according to claim 4 , having a thickness of 10 to 5000 μm.
7. The multilayer structure according to claim 4 , in a packaging material to be subjected to hot water treatment.
8. A method for producing a resin composition pellet comprising melt-mixing (A) a saponified ethylene-vinyl ester copolymer with (B) a completely dehydrated magnesium sulfate, and a polyamide resin
wherein the content ratio (B/A) of component (B) to component (A) is in the range of 50/50 to 1/99 in terms of weight ratio, and
wherein the amount of the polyamide resin is 1 to 30% by weight based on the weight of component (A).
9. A method for producing a melt-molded article comprising:
melting a resin composition comprising (A) a saponified ethylene-vinyl ester copolymer, (B) a completely dehydrated magnesium sulfate, and a polyamide resin, and
forming into a molded article of the resin composition,
wherein the content ratio (B/A) of component (B) to component (A) is in the range of 50/50 to 1/99 in terms of weight ratio, and
wherein the amount of the polyamide resin is 1 to 30% by weight based on the weight of component (A).
10. The multilayer structure according to claim 5 , having a thickness of 10 to 5000 μm.
11. The multilayer structure according to claim 5 , in a packaging material to be subjected to hot water treatment.
12. The method according to claim 8 , wherein the melt-mixing is performed while suppressing a viscosity increase of the resin composition.
13. The method according to claim 9 , wherein the melting is performed under suppressing a viscosity increase of the resin composition.