Coated article with low-E coating including tin oxide interlayer
View Patent ↗A coated article is provided which may be heat treated (e.g., thermally tempered) in certain instances. In certain example embodiments, an interlayer of or including a metal oxide such as tin oxide is provided under an infrared (IR) reflecting layer so as to be located between respective layers comprising silicon nitride and zinc oxide. It has been found that the use of such a tin oxide inclusive interlayer results in significantly improved mechanical durability, thermal stability and/or haze characteristics.
1. A coated article including a coating supported by a glass substrate, the coating comprising:
a first dielectric layer;
a layer comprising zinc oxide on the glass substrate over at least the first dielectric layer;
a first IR reflecting layer;
a second IR reflecting layer;
a dielectric film located between at least the first and second IR reflecting layers;
another dielectric film located above the first and second IR reflecting layers;
wherein the dielectric film located between the first and second IR reflecting layers comprises first and second layers comprising tin oxide that are spaced apart by at least a layer comprising silicon nitride; and
wherein each of the first and second layers comprising tin oxide consist essentially of tin oxide.
2. The coated article of claim 1 , wherein another layer comprising zinc oxide is located below and directly contacting the second IR reflecting layer.
3. The coated article of claim 1 , wherein a layer comprising an oxide of titanium is located between the glass substrate and the first dielectric layer.
4. The coated article of claim 1 , wherein a layer comprising an oxide of NiCr is located over and directly contacting the first IR reflecting layer.
5. The coated article of claim 1 , where said another dielectric film located above the first and second IR reflecting layers comprises a layer comprising silicon nitride located over a layer comprising tin oxide.
6. The coated article of claim 1 , where said another dielectric film located above the first and second IR reflecting layers comprises a layer comprising tin oxide.
7. The coated article of claim 1 , wherein, said first layer comprising tin oxide is closer to the glass substrate than is the second layer comprising tin oxide, and wherein said first layer comprising tin oxide is thicker than the second layer comprising tin oxide.
8. The coated article of claim 7 , wherein said first layer comprising tin oxide is from 200-700 angstroms thick and said second layer comprising tin oxide is from 50-200 angstroms thick.
9. The coated article of claim 1 , wherein neither said first nor second layer comprising tin oxide contacts a layer comprising silver.
10. The coated article or claim 1 , wherein said IR reflecting layers comprise silver.
11. The coated article of claim 1 , wherein the first and second layers comprising tin oxide each directly contact the layer comprising silicon nitride.
12. The coated article of claim 1 , wherein said layer comprising zinc oxide is located directly under and contacting the first IR reflecting layer.