Aqueous coating material and painted article
View Patent ↗The present invention relates to an aqueous coating material containing polymer (I), colloidal silica (II), and nonionic surfactant (III) with an HLB value of 16 or more. The polymer (I) is obtained by copolymerization of monomer mixture (M) that contains 0.2 to 10% by mass of monomer (a) having two or more radically polymerizable groups. The solid content of the colloidal silica (II) is 0.1 to 20 parts by mass with respect to 100 parts by mass of the polymer (I). The content of the nonionic surfactant (III) is 0.01 to 10 parts by mass with respect to 100 parts by mass of the polymer (I). The present invention also relates to a painted article where the aqueous coating material is applied. Therefore, an aqueous coating material and a painted article capable of expressing stain resistance and weather resistance can be provided by reducing a water contact angle.
1. An aqueous coating material, comprising:
a polymer (I);
colloidal silica (II); and
a nonionic surfactant (III) having an HLB value of 16 or more,
wherein the polymer (I) is obtained by a process comprising polymerizing a monomer mixture (M) comprising 0.2 to 10% by mass of monomer (a) comprising 2 or more radically polymerizable groups,
a solid content of the colloidal silica (II) is 0.1 to 20 parts by mass with respect to 100 parts by mass of the polymer (I), and
a content of the nonionic surfactant (III) is 0.01 to 10 parts by mass with respect to 100 parts by mass of the polymer (I).
2. The aqueous coating material of claim 1 , wherein the polymer (I) has an average particle size of 80 to 140 nm, and the monomer mixture (M) comprises 0.1 to 9% by mass of acrylic acid.
3. The aqueous coating material of claim 1 , wherein the monomer mixture (M) comprises a monomer mixture (m1) that comprises the monomer (a) and a monomer mixture (m2) that does not comprise the monomer (a), the polymerizing comprises, polymerizing the monomer mixture (m1), and then polymerizing the monomer mixture (m2), and
a polymer comprising the monomer mixture (m2) has a glass transition temperature of 20° C. or more calculated from a FOX equation.
4. The aqueous coating material of claim 1 , wherein the monomer mixture (M) comprises a monomer mixture (m1) that comprises the monomer (a) and a monomer mixture (m2) that does not comprise the monomer (a),
the polymerizing comprises, polymerizing the monomer mixture (m1), and then polymerizing the monomer mixture (m2), and
a polymer comprising a monomer mixture other than the monomer mixture (ml) has a glass transition temperature of 60° C. or less calculated from a FOX equation.
5. The aqueous coating material of claim 1 , further comprising an anionic surfactant comprising a phosphoric acid structure.
6. A painted article obtained by a process comprising contacting an article with a paint comprising an aqueous coating material of claim 1 .
7. The aqueous coating material of claim 2 , wherein the monomer mixture (M) comprises a monomer mixture (m1) that comprises the monomer (a) and a monomer mixture (m2) that does not comprise the monomer (a),
the polymerizing comprises, polymerizing the monomer mixture (m1), and then polymerizing the monomer mixture (m2), and
a polymer comprising the monomer mixture (m2) has a glass transition temperature of 20° C. or more calculated from a FOX equation.
8. The aqueous coating material of claim 2 , wherein the monomer mixture (M) comprises a monomer mixture (m1) that comprises the monomer (a) and a monomer mixture (m2) that does not comprise the monomer (a),
the polymerizing comprises, polymerizing the monomer mixture (m1), and then polymerizing the monomer mixture (m2), and
a polymer comprising a monomer mixture other than the monomer mixture (m1) has a glass transition temperature of 60° C. or less calculated from a FOX equation.
9. The aqueous coating material of claim 1 , wherein the monomer mixture (M) comprises 0.4% to 10% by mass of monomer (a).
10. The aqueous coating material of claim 1 , wherein the monomer mixture (M) comprises 0.2 to 3% by mass of monomer (a).
11. The aqueous coating material of claim 9 , wherein the monomer mixture (M) comprises 0.4% to 3% by mass of monomer (a).
12. The aqueous coating material of claim 2 , wherein the polymer (I) has an average particle size of 100 to 130 nm
13. The aqueous coating material of claim 1 , wherein the solid content of the colloidal silica (II) is 0.5 to 18 parts by mass with respect to 100 parts by mass of the polymer (I).
14. The aqueous coating material of claim 1 , wherein the solid content of the colloidal silica (II) is 1 to 10 parts by mass with respect to 100 parts by mass of the polymer (I)
15. The aqueous coating material of claim 1 , wherein the colloidal silica (II) has an average particle size of 1 to 60 nm.
16. The aqueous coating material of claim 1 , wherein the colloidal silica (II) has an average particle size of less than 40 nm.
17. The aqueous coating material of claim 1 , wherein the colloidal silica (II) has an average particle size of less than 20 nm.
18. The aqueous coating material of claim 1 , wherein the nonionic surfactant (III) has an HLB value of 17 or more.
19. The aqueous coating material of claim 1 , wherein the nonionic surfactant (III) has an HLB value of 18 or more.
20. The aqueous coating material of claim 1 , wherein the content of the nonionic surfactant (III) is 0.3 to 5 parts by mass with respect to 100 parts by mass of the polymer (I).