Copper red frits and pigments comprising silica and at least one of cupric oxide and cuprous oxide
View Patent ↗This invention relates to lead free and cadmium free copper-containing glass fits that can be used as pigments to color other glass fits or to impart color to solid substrates such as glass, ceramic or metals, or to impart color to a thermoplastic mass. The compositions comprise silica, alkali metal oxides, alkaline earth metal oxides, tin oxide and copper oxide. The resulting compositions can be used to decorate and protect automotive, beverage, architectural, pharmaceutical and other glass substrates, generally imparting a red color.
1. An enamel composition that is free of lead, cadmium, bismuth, iron, selenium, arsenic, tantalum, chromium and sulfides, the composition comprising a solids portion comprising a frit portion, wherein the frit portion comprises, prior to firing:
a. 50-75 wt % SiO 2 ,
b. 4-22 wt % R 2 O, wherein R is at least one of Na and K,
c. 2-30 wt % R′O, wherein R′ is at least one of Mg, Ca, Sr and Ba,
d. 0.5-20 wt % B 2 O 3 ,
e. 1-15 wt % SnO, and
f. 2-10 wt % of at least one of Cu 2 O and CuO.
2. The composition of claim 1 , wherein the frit portion further comprises 0.1-5 wt % Fe 2 O 3 .
3. The composition of claim 1 , wherein R 2 O comprises 0.3-18 wt % Na 2 O and sufficient K 2 O to bring the total Na 2 O+K 2 O to 4-22%.
4. The composition of claim 1 , wherein the frit portion comprises, prior to firing:
a. 50-70 wt % SiO 2 ,
b. 6-20 wt % R 2 O,
c. 3-12 wt % CaO,
d. 0-12 wt % MgO,
e. 5-15 wt % B 2 O 3 ,
f. 0-12 wt % Al 2 O 3 ,
g. 2-12 wt % SnO, and
h. 2-10 wt % of at least one of Cu 2 O and CuO.
5. The composition of claim 4 , wherein R 2 O comprises 3-15 wt % Na 2 O and sufficient K 2 O to bring the total Na 2 O+K 2 O to 6-20%.
6. A substrate bearing a fired coating of the composition of claim 1 .
7. The composition of claim 1 , wherein the frit portion further comprises 0.5-20 wt % of a reducing agent selected from the group consisting of reducing sugars, potassium sodium tartrate, organic compounds, organic salts, carbon black and combinations thereof.
8. The composition of claim 1 , wherein the frit portion comprises, prior to firing:
a. 50-70 wt % SiO 2 ,
b. 6-20 wt % R 2 O,
c. 2-24 wt % R′O,
d. 5-16 wt % B 2 O 3 ,
e. 2-12 wt % SnO,
f. 2-10 wt % of at least one of Cu 2 O and CuO, and further comprises
g. 0-12 wt % Al 2 O 3 .
9. The composition of claim 1 , wherein the frit portion comprises, prior to firing:
a. 50-75 wt % SiO 2 ,
b. 4-22 wt % R 2 O, wherein R is at least one of Na and K,
c. 2-30 wt % R′O, wherein R′ is at least one of Mg, Ca, Sr and Ba,
d. 0.5-20 wt % B 2 O 3 ,
e. 3-15 wt % SnO, and
f. 2-10 wt % of at least one of Cu 2 O and CuO.
10. A method of making a red glass frit pigment composition comprising
a. smelting a glass by heating a mixture of compounds that provide the following oxides:
i. 50-75 wt % SiO 2 ,
ii. 4-22 wt % R 2 O, wherein R is at least one of Na and K,
iii. 2-30 wt % R′O, wherein R′ is at least one of Mg, Ca, Sr and Ba,
iv. 0.5-20 wt % B 2 O 3 ,
v. 1-15 wt % SnO, and
vi. 2-10 wt % of at least one of Cu 2 O and CuO,
b. cooling the glass,
c. annealing, to increase the color strength, if necessary, and
d. reducing the glass to a desired particle size by mechanical grinding or milling.
11. A particulate red pigment composition comprising the glass frit produced by the process of claim 10 , said glass frit having a D 90 particle size of less than 10 microns.
12. A method of manufacturing red glass comprising adding a coloring frit, to a mass of molten colorless glass in a feeder channel, forming glass objects from the molten mass of glass, then subjecting the glass objects to heat treatment so that they develop a red color, wherein the coloring frit is free of lead, cadmium, bismuth, iron, selenium, arsenic, tantalum, chromium and sulfides, and wherein the coloring frit comprises:
a. 50-75 wt % SiO 2 ,
b. 4-22 wt % R 2 O, wherein R is at least one of Na and K,
c. 2-30 wt % R′O, wherein R′ is at least one of Mg, Ca, Sr and Ba,
d. 0.5-20 wt % B 2 O 3 ,
e. 1-15 wt % SnO, and
f. 2-10 wt % of at least one of Cu 2 O and CuO.
13. The method of claim 12 , wherein the partial pressure of oxygen in the molten mass of glass is less than 10 −9 atmospheres.
14. A method of decorating a thermoplastic mass, comprising
a. forming a red-colored enamel composition enamel composition that is free of lead, cadmium, iron, bismuth, selenium, arsenic, tantalum, chromium and sulfides, the composition comprising a solids portion comprising a frit portion, wherein the frit portion comprises, prior to firing:
b. 50-75 wt % SiO 2 ,
c. 8-25 wt % R 2 O, wherein R is at least one of Li, Na and K,
d. 2-30 wt % R′O, wherein R′ is at least one of Mg, Ca, Sr and Ba,
e. 1-15 wt % SnO, and
f. 2-10 wt % of at least one of Cu 2 O and CuO, and
g. blending the enamel composition with a thermoplastic mass to form a red-colored thermoplastic mass.
15. The method of claim 12 , wherein the mass of molten colorless glass has a partial pressure of oxygen in the molten mass of greater than 10 −4 to less than 10 −1 atmospheres.