Method for welding shafts on vertical rotational axis
View Patent ↗A first tubular, inner radial annular seam is produced to weld together two hollow cylinders by narrow-gap tungsten inert gas arc welding. Narrow-gap metal gas-shielded arc welding is used to create another tubular, outer radial annular seam to further weld together both hollow cylinders. In this manner, the rotational axis of the rotor shaft remains vertically aligned throughout the entire production method of welding together the shaft parts. In this manner, the required production time can be advantageously reduced and the use of welding filler can be effectively decreased.
1. A method for joint welding a shaft, particularly for a turbine and/or a generator, comprising:
providing shaft parts, symmetrical about and coaxial along a vertical rotational axis, including at least two hollow cylinders;
positioning two of the shaft parts coaxially to each other along the vertical rotational axis, with annular surfaces of two hollow cylinders abutting each other;
forming a tubular inner radial annular seam to weld together the two hollow cylinders in a radial inner region of the annular surfaces by narrow-gap tungsten inert gas arc welding; and
forming a tubular outer radial annular seam after said forming of the tubular inner radial annular seam to further weld together the two hollow cylinders in an outer radial region of the annular surfaces by narrow-gap metal gas-shielded arc welding, while the vertical rotational axis remains vertically aligned.
2. The method as claimed in claim 1 , wherein the tubular outer radial annular seam is welded immediately after the tubular inner radial annular seam between two shaft parts is welded.
3. The method as claimed in claim 1 , further comprising forming a tubular middle radial annular seam to further weld together the hollow cylinders by narrow-gap tungsten inert gas welding, after said forming of the tubular inner radial annular seam and before said forming of the tubular outer radial annular seam.
4. The method as claimed in claim 3 , wherein said forming of the tubular middle radial annular seam is repeated for all of the shaft parts of the entire rotor shaft prior to said forming of the tubular outer radial annular seams of all of the shaft parts.
5. The method as claimed in claim 4 , wherein the tubular middle radial annular seam is radially 2 mm to 20 mm thick.
6. The method as claimed in claim 5 , wherein the narrow-gap metal gas-shielded arc welding is one of narrow-gap metal inert gas arc welding and narrow-gap metal active gas arc welding.