Method and apparatus for defibrillating cellulose fibers
View Patent ↗The current invention is directed to a method and apparatus for defibrillating cellulose fibers achieved through single or multiple passes of raw or pre-processed cellulose fiber slurry with a preferred solid material consistency range of 35% to 55% through twin-screw fiber processing machines. During this processing operation fiber slurries are optionally further enhanced with additional fiber and mineral additives to optimize performance of the material for specific end purposes. The hyper defibrillated fiber slurry produced can be defined as one reaching a Schopper-Riegler (SR) level between 75 SR and 85 SR and/or producing a pressed, dried board with a density of preferably at least 850 kg/m 3 .
1. Method for the treatment of a composition comprising cellulose fibres into a composition comprising cellulose microfibers, said method comprises the steps of:
a) Providing a composition comprising fibres;
b) Admixing aqueous solution/solvent to said composition comprising cellulose fibres to provide a pulp suspension comprising cellulose fibres;
c) Feeding said pulp suspension comprising cellulose fibres into a mechanical defibrillation process using a refining twin screw;
d) Refining said pulp suspension comprising cellulose fibres with at least the use of said refining twin screw, to provide a composition comprising cellulose microfibers,
e) wherein in step b) the pulp suspension has a consistency of between 45% and 55%, and the composition comprising cellulose microfibers has a Schopper-Riegler value (SR) upon leaving the twin screw of step c) of at least 80° SR.
2. The method according to claim 1 wherein said composition comprising cellulose microfibers at the end of the refining step has a density of at least 850 kg/m 3 .
3. The method according to claim 1 wherein said composition comprising cellulose microfibers has a density of between, and including, 1000 kg/m 3 and 1450 kg/m 3 .
4. The method according to claim 1 wherein the composition comprising cellulose microfibers has a Schopper-Riegler value (SR) before any drying and upon leaving the twin-screw of the process, of between and including 80° SR and 90° SR.
5. The method according to claim 1 wherein the composition comprising cellulose fibres of step a) is selected from the group consisting of paper, waste paper, and recycled paper.
6. The method according to claim 1 , comprising a further step of adding one or more further additives after the refining step.
7. The method according to claim 6 , wherein the further additives are selected from the group comprising mineral and organic fillers, flow modifiers, sizing agents, dyes, coloured pigments and mordents.
8. Method according to claim 1 , wherein the refining twin screw is a co-rotating twin screw or a counter-rotating twin screw.
9. Method according to claim 1 , further comprising the step of moulding a 2- or 3-dimensional shaped body from said composition comprising cellulose microfiber stock.
10. Method according to claim 1 further comprising the step of moulding of a sheet from said composition comprising cellulose microfibers and attaching said sheet to a carrier to form a flooring tile.
11. A method according to claim 1 wherein the fibres are introduced dry and inlets are provided to introduce liquid to be combined with the fibres.
12. The method according to claim 1 wherein said composition comprising cellulose microfibers has a density of between, and including, 1150 kg/m 3 and 1400 kg/m 3 .
13. The method according to claim 1 wherein said composition comprising cellulose microfibers has a density of between, and including, 1300 kg/m 3 and 1400 kg/m 3 .
14. The method according to claim 1 wherein the composition comprising cellulose microfibers has a Schopper-Riegler value (SR) before any drying and upon leaving the twin-screw of the process, of between and including 80° SR and 88° SR.