Method for producing martensitic steel with mixed hardening
View Patent ↗A method of producing a martensitic steel including a content of other metals such that it can be hardened by intermetallic compound and carbide precipitation, with an Al content of between 0.4% and 3%. The heat shaping temperature of a last heat shaping pass of the steel is lower than the solubility temperature of aluminum nitrides in the steel, and a treatment temperature for each potential heat treatment after the last heat shaping pass is lower than the solid-state solubility temperature of the aluminum nitrides in the steel.
1. A method for producing martensitic steel that comprises alloying elements such that the steel can be hardened by an intermetallic compound and carbide precipitation, with an Al content of between 0.4% and 3%, the method comprising:
subjecting the steel to heat shaping, wherein:
a heat shaping temperature for a last heat shaping pass is less than solid-state solubility temperature of aluminum nitrides in the steel;
a heat shaping temperature of each of the heat shaping passes preceding a last heat shaping pass is less than the solid-state solubility temperature of the aluminum nitrides in the steel; and
the heat treatment temperature for each optional heat treatment after the last heat shaping pass is less than the solid-state solubility temperature of the aluminum nitrides in the steel.
2. The production method according to claim 1 , wherein the Al content of the steel is between 0.5% and 2%.
3. The production method according to claim 1 , wherein in the steel, the C content is less than 0.4%, the Cr content is between 0.5% and 7%, the Ni content is between 6% and 18%, the Co content is between 4% and 18%.