COMPOSITION BASED ON NATURAL RUBBER AND A POLYAMINE COMPOUND

1 . Reinforced rubber composition based at least (a) on an elastomeric matrix comprising non-halogenated natural rubber, (b) on a reinforcing filler, (c) on a primary polyamine compound having at least two primary amine functions corresponding to formula 1 or 2 below:

in which:

R 1 and R 2 , which are identical or different, are selected from the group consisting of alkylidenes having from 1 to 20 carbon atoms, cycloalkylidenes having from 5 to 24 carbon atoms, arylidenes having from 6 to 18 carbon atoms, aralkylidenes having from 7 to 25 carbon atoms and heterocycles, which are identical or different, having from 4 to 25 carbon atoms;

R 3 and R 4 , which are identical or different, are selected from the group consisting of alkylidenes having from 1 to 20 carbon atoms, alkylidynes having from 1 to 20 carbon atoms, alkylylidynes having from 1 to 20 carbon atoms, cycloalkylidenes having from 5 to 24 carbon atoms, cycloalkylidynes having from 5 to 24 carbon atoms, cycloalkylylidynes having from 5 to 24 carbon atoms, arylidenes having from 6 to 18 carbon atoms, arylidynes having from 6 to 18 carbon atoms, arylylidynes having from 6 to 18 carbon atoms, aralkylidenes having from 7 to 25 carbon atoms, aralkylidynes having from 6 to 18 carbon atoms, aralkylylidynes having from 6 to 18 carbon atoms, and heterocycles, which are identical or different, having from 4 to 25 carbon atoms;

R 3 optionally comprises one or more identical or different heteroatom(s), chosen from O, N, S and Si;

m is equal to 1, 2 or 3;

n is equal to 1, 2 or 3,

in an amount between 0 and 7 mmol per 100 g of elastomer.

2 . Rubber composition according to claim 1 , wherein the polyamine compound is present in an amount preferably ranging from 1 to 6 mmol.

3 . Rubber composition according to claim 1 , wherein the natural rubber in the elastomeric matrix is present in a weight fraction of greater than or equal to 50% by weight of the total weight of the matrix.

4 . Rubber composition according to claim 3 , wherein the elastomeric matrix consists of 100% natural rubber.

5 . Rubber composition according to claim 1 , wherein the reinforcing filler comprises an organic filler in a proportion of 100% by weight of the total weight of the composition.

6 . Rubber composition according to claim 1 , wherein the reinforcing filler comprises an inorganic filler and further comprising a coupling agent.

7 . Rubber composition according to claim 1 , wherein the reinforcing filler comprises a reinforcing inorganic filler in proportions ranging from 55% to 100% by weight of the total weight of the composition.

8 . Rubber composition according to claim 1 , wherein the polyamine compound having at least two primary amine functions is chosen from the group consisting of diamines, triamines and tetraamines.

9 . Rubber composition according to claim 8 , wherein the polyamine compound having at least two primary amine functions is chosen from the group consisting of 1,6-hexamethylenediamine, 1,8-octamethylenediamine, 1,4-diaminocyclohexane, 1,2-diaminocyclohexane, N,N-bis(2-aminoethyl)ethane-1,2-diamine.

10 . Process for the preparation of a reinforced rubber composition as described in claim 1 , comprising:

(i) carrying out, at a maximum temperature of between 130° C. and 200° C., a first step of thermomechanical working of the necessary base constituents of the rubber composition, with the exception of the crosslinking system, by intimately incorporating, by kneading, ingredients of the composition in the elastomeric matrix based on natural rubber, then

(ii) carrying out, at a temperature lower than said maximum temperature of said first step, preferably of less than 110° C., a second step of mechanical working during which said crosslinking system is incorporated,

wherein, prior to carrying out the abovementioned stage (i), the process comprises the stages of the manufacture of natural rubber comprising a stage of addition of the primary polyamine compound corresponding to formula 1 or 2.

11 . Process for the preparation of a reinforced rubber composition as described in claim 1 , comprising:

(i) carrying out, at a maximum temperature of between 130° C. and 200° C., a first step of thermomechanical working of the necessary base constituents of the rubber composition, with the exception of the crosslinking system, by intimately incorporating, by kneading, ingredients of the composition in the elastomeric matrix based on natural rubber, then

(ii) carrying out, at a temperature lower than said maximum temperature of said first step, preferably of less than 110° C., a second step of mechanical working during which said crosslinking system is incorporated,

wherein, prior to carrying out the abovementioned stage (i), the process comprises a stage of preparation of a masterbatch based on non-halogenated natural rubber and on the primary polyamine compound.

12 . Process for the preparation of a reinforced rubber composition as described in claim 1 , comprising:

(i) carrying out, at a maximum temperature of between 130° C. and 200° C., a first step of thermomechanical working of the necessary base constituents of the rubber composition, with the exception of the crosslinking system, by intimately incorporating, by kneading, ingredients of the composition in the elastomeric matrix based on natural rubber, then

(ii) carrying out, at a temperature lower than said maximum temperature of said first step, preferably of less than 110° C., a second step of mechanical working during which said crosslinking system is incorporated,

wherein the primary polyamine compound is added directly during stage (i) with the other compounds of the composition.

13 . Process for the preparation of a tire component according to claim 10 , wherein the primary polyamine compound is added in a small proportion of between 0 and 7 mmol per 100 g of elastomer.

14 . Tire semi-finished rubber product, comprising a crosslinkable or crosslinked rubber composition according to claim 1 .

15 . Tire, comprising a semi-finished product according to claim 14 .

16 . Rubber composition according to claim 5 , wherein the organic filler comprises carbon black.

17 . Rubber composition according to claim 6 , wherein the inorganic filler comprises a reinforcing silica.