FERRITIC STAINLESS STEEL FOR EGR COOLER AND EGR COOLER
A ferritic stainless steel suitable for use as an EGR cooler member, which can be Ni-brazed into an EGR cooler, contains, by mass, C: at most 0.03%, Si: from more than 0.1 to 3%, Mn: from 0.1 to 2%, Cr: from 10 to 25%, Nb: from 0.3 to 0.8%, and N: at most 0.03%, and optionally selectively contains (a) one or more of Mo, Cu, V and W in a total amount of at most 4%, (b) one or more of Ti, Al and Zr in a total amount of at most 0.3%, (c) one or more of Ni and Co in a total amount of at most 5%, and (d) one or more of REMs (rare earth metals) and Ca in a total amount of at most 0.2%, with a balance of Fe and inevitable impurities.
1 . A ferritic stainless steel for EGR cooler members, which contains, by mass, C: at most 0.03%, Si: from more than 0.1 to 3%, Mn: from 0.1 to 2%, Cr: from 10 to 25%, Nb: from 0.3 to 0.8%, and N: at most 0.03%, with a balance of Fe and inevitable impurities.
2 . The ferritic stainless steel as claimed in claim 1 , further containing one or more of Mo, Cu, V and W in a total amount of at most 4%.
3 . The ferritic stainless steel as claimed in claim 1 , further containing one or more of Ti, Al and Zr in a total amount of at most 0.3%.
4 . The ferritic stainless steel as claimed in claim 1 , further containing one or more of Ni and Co in a total amount of at most 5%.
5 . The ferritic stainless steel as claimed in claim 1 , further containing one or more of REMs (rare earth metals) and Ca in a total amount of at most 0.2%.
6 . The ferritic stainless steel as claimed in claim 1 , wherein the total content of C and N is at least 0.01% by mass.
7 . An EGR cooler comprising constitutive members formed of a steel material of the steel of claim 1 , in which at least the members are joined with the other member by Ni-brazing.
8 . An EGR cooler, in which the members to be in contact with both vehicle exhaust gas and cooling water are formed of a steel material of the steel of claim 1 , and in which at least the members are joined with the other member by Ni-brazing.