Mineral fibres and their use
The invention relates to mineral fibers formed of a composition comprising the following oxides, by weight of composition: —SiO 2 35 to 43.5% —Al 2 O 3 18 to 22% —Fe 2 O 3 9 to 16% —CaO 8 to 17% —MgO 7 to 15% —Na 2 O+K 2 O 1 to 5% —MnO up to 2%.
1. Mineral fibres formed of a composition comprising the following oxides, by weight of composition:
SiO 2
35 to 43.5%
Al 2 O 3
18 to 22%
Fe 2 O 3
at least 12.5 to 16%
CaO
8 to 17%
MgO
at least 11 to 15%
Na 2 O + K 2 O
1 to 5%: and
MnO
up to 2%.
2. Mineral fibres according to claim 1 in which the content of CaO is not more than 16%.
3. Mineral fibres according to claim 1 in which the composition further comprises TiO 2 in an amount of up to 4%.
4. Mineral fibres according to claim 1 in which the composition further comprises P 2 O 5 in an amount of up to 4%.
5. Mineral fibres according to claim 1 in which the content of MnO is at least 0 2%.
6. Mineral fibres according to claim 1 in which the content of Na 2 O is in the range 1 to 4%.
7. Mineral fibres according to claim 1 in which the content of K 2 O is in the range 0.5 to 2%.
8. Mineral fibres according to claim 1 in which the content of SiO 2 is not more than 42%.
9. Mineral fibres according to claim 8 in which the content of SiO 2 is not more than 40%.
10. Mineral fibres according to claim 1 in which the content of SiO 2 +Al 2 O 3 is not more than 60%.
11. A product formed of mineral fibres according to claim 1 in coherent form.
12. A method of using a bonded product formed of the mineral fibres of claim 11 for fire protection, comprising fitting the bonded product around or against an element which is to be insulated or protected.
13. The method according to claim 12 in an application where there is a risk of explosive fire.
14. The method according to claim 13 in which the density of the mineral fibre product is not more than 200 kg/m 3 .
15. The method according to claim 12 in an off-shore application or a marine application or as tunnel insulation or in a chemical plant.
16. The method according to claim 12 in which the thickness of the mineral fibre product is not more than 300 mm.
17. A bonded product formed of mineral fibres according to claim 1 in consolidated form with binder.
18. A method of making mineral fibres according to claim 1 comprising providing a mineral charge, melting the charge to produce a mineral melt and fiberising the melt.
19. A method according to claim 18 in which fiberisation is carried out using a cascade spinning method.