Non-heat treated rolled steel and drawn wire rod with excellent toughness, and method for manufacturing the same
There is provided a rolled steel with excellent toughness, a drawn wire rod prepared by drawing the rolled steel, and a method for manufacturing the same, in which even if a heating step is omitted, the toughness of the steel can be improved by securing a degenerated pearlite structure in an internal structure of the rolled steel by controlling a content of Mn among components and cooling conditions, and then preventing C diffusion. The rolled steel according to the present invention includes C: 0.15˜0.30%, Si: 0.1˜0.2%, Mn: 1.8˜3.0%, P: 0.035% or less, S: 0.040% or less, the remainder Fe, and other inevitable impurites, as a percentage of weight, in which the microstucture of the rolled steel is composed of ferrite and pearlite including cementite with 150 nm or less of thickness.
1. A non-heat treated rolled steel with excellent toughness, comprising C: 0.15˜0.30%, Si: 0.1˜0.2%, Mn: 1.8˜3.0%, P: 0.035% or less, S: 0.040% or less, the remainder Fe, and other inevitable impurities, as a percentage of weight, wherein microstuctures in the non-heat treated rolled steel are composed of 40-60% of pearlite and the remainder ferrite, and wherein the pearlite is a degenerated pearlite.
2. The non-heat treated rolled steel with excellent toughness of claim 1 , wherein the pearlite includes cementite with 150 nm or less of thickness.
3. The non-heat treated rolled steel with excellent toughness of claim 1 , wherein an aspect ratio (width:thickness) of the cementite included in the pearlite is 30:1 or less.
4. The non-heat treated rolled steel with excellent toughness of claim 1 , wherein the cementite included in the pearlite has a discontinuous form.
5. The non-heat treated rolled steel with excellent toughness of claim 1 , wherein the rolled steel has 650˜750 MPa of a tensile strength and 60˜70% of a reduction in area (RA).
6. A non-heat treated drawn wire rod with excellent toughness produced by cold drawing the rolled steel of claim 1 , wherein the drawn wire rod has 800˜900 MPa of a tensile strength.
7. A method for manufacturing a non-heat treated rolled steel with excellent toughness, comprising:
heating a billet that includes C: 0.15˜0.30%, Si: 0.1˜0.2%, Mn: 1.8˜3.0%, P: 0.35% or less, S: 0.040% or less, the remainder Fe, and other inevitable impurities, as a percentage of weight, to the range of A e3 +150° C.˜A e3 +250° C.;
primarily cooling the heated billet to the range of A e3 +50° C.˜A e3 +100° C., wherein the cooling rate is in the range of 5˜15° C./s;
manufacturing the rolled steel by rolling the cooled billet at A e3 +50° C.˜A e3 +100° C.; and
secondarily cooling the rolled steel to a temperature of 600° C. or less.
8. The method for manufacturing a non-heat treated rolled steel with excellent toughness of claim 7 , wherein the heating of the billet in the heating step is performed for 30 minutes to 1 and a half hours.
9. The method for manufacturing a non-heat treated rolled steel with excellent toughness of claim 7 , wherein the cooling rate in the secondary cooling step is in the range of 0.5˜1.5° C./s.
10. A method for manufacturing a non-heat treated drawn wire rod with excellent toughness, comprising: cold drawing the rolled steel of claim 7 .