Composition for film having prism-type retroreflection structure formed on the surface thereof

1. An acrylic film, which was obtained from a composition comprising:

(A) an acrylic polymer produced by polymerizing (a-2) a monomer component in the presence of (A-1) a crosslinked acrylic polymer; and (B) a thermoplastic acrylic polymer,

the composition having a fluidity (MFR: measured under heating at 230° C. and compression at 37.3 N) of 1 to 14, and

the composition having a gel content of 25 to 50% by weight with respect to 100% by weight in total of the acrylic polymer (A) and the thermoplastic acrylic polymer (B);

the film having a prism type retroreflection structure formed on the surface thereof.

2. The acrylic film according to claim 1 , wherein

the acrylic polymer (A) is produced by polymerizing the monomer component (a-2) comprising not less than 80% by weight of a methacrylic acid ester, and 20 to 0% by weight of at least one selected from an acrylic acid ester and other copolymerizable vinyl monomer, in the presence of the crosslinked acrylic polymer (A-1);

the acrylic polymer (A) is in a particulate form having a weight average particle diameter of 300 to 3,000 Å;

the acrylic polymer (A) has a reduced viscosity (as measured with a 0.3% solution in N,N′-dimethylformamide at 30° C.) of methyl ethyl ketone (MEK) soluble-matter being not greater than 0.35 dl/g; and

the crosslinked acrylic polymer (A-1) is produced by copolymerizing a monomer component (a-1) comprising an acrylic monomer and a polyfunctional monomer having two or more nonconjugated double bonds per molecule and being capable of copolymerizing with the acrylic monomer, and has a single-layer or multilayer structure.

3. The acrylic film according to claim 2 , wherein the monomer component (a-1) comprises the polyfunctional monomer in an amount of 0.2 to 2 parts by weight with respect to 100 parts by weight of the monomer(s) other than the polyfunctional monomer.

4. The acrylic film according to claim 2 wherein the graft rate of the monomer component (a-2) to the crosslinked acrylic polymer (A-1) is 50 to 140% by weight.

5. The acrylic film according to claim 2 , wherein each layer constituting the crosslinked acrylic polymer (A-1) has a glass transition temperature of less than 0° C.

6. The acrylic film according to claim 1 , wherein the thermoplastic acrylic polymer (B) comprises

(B1) a thermoplastic acrylic polymer that is produced by copolymerizing a monomer component comprising not less than 95% by weight of a methacrylic acid ester and not greater than 5% by weight of at least one selected from an acrylic acid ester and other copolymerizable vinyl monomer, and exhibits a fluidity of not greater than 8 (MFR: measured under heating at 230° C. and compression at 37.3 N), and

(B2) a thermoplastic acrylic polymer that is produced by copolymerizing a monomer component comprising not less than 92% by weight of a methacrylic acid ester and not greater than 8% by weight of at least one selected from an acrylic acid ester and other copolymerizable vinyl monomer, and exhibits a fluidity of not less than 15 (MFR: measured under heating at 230° C. and compression at 37.3 N),

wherein the weight ratio of the (B1)/(B2) is 10/90 to 90/10.

7. The acrylic film according to claim 1 , wherein the thermoplastic acrylic polymer (B) is (B3) a thermoplastic acrylic polymer that is produced by copolymerizing a monomer component comprising not less than 80% by weight of a methacrylic acid ester and 0 to 20% by weight of at least one selected from an acrylic acid ester and other copolymerizable vinyl monomer, and has a reduced viscosity of not greater than 0.35 dl/g (as measured with a 0.3% solution in N,N′-dimethylformamide at 30° C.).

8. The acrylic film according to claim 1 , wherein the composition has a Vicat softening temperature of not less than 85° C.

9. An acrylic film, which was obtained from a composition comprising the following acrylic polymer (A), the following thermoplastic acrylic polymer (B1) and the following thermoplastic acrylic polymer (B2),

the weight ratio of the (B1)/(B2) being 10/90 to 90/10, and

the gel content being 25 to 50% by weight with respect to 100% by weight in total of the acrylic polymer (A), the thermoplastic acrylic polymer (B1) and the thermoplastic acrylic polymer (B2),

acrylic polymer (A):

being produced by polymerizing a monomer component (a-2) comprising not less than 80% by weight of a methacrylic acid ester, and 20 to 0% by weight of at least one selected from an acrylic acid ester and other copolymerizable vinyl monomer, in the presence of a crosslinked acrylic polymer (A-1),

being in a particulate form having a weight average particle diameter of 300 to 3,000 Å, and

having a reduced viscosity (as measured with a 0.3% solution in N,N′-dimethylformamide at 30° C.) of methyl ethyl ketone (MEK) soluble-matter being not greater than 0.35 dl/g,

wherein, the crosslinked acrylic polymer (A-1) is produced by copolymerizing a monomer component (a-1) comprising an acrylic acid ester and a polyfunctional monomer having two or more nonconjugated double bonds per molecule and being capable of copolymerizing with the acrylic acid ester, and has a single-layer or multilayer structure;

thermoplastic acrylic polymer (B1):

being produced by copolymerizing a monomer component comprising not less than 95% by weight of a methacrylic acid ester and not greater than 5% by weight of at least one selected from an acrylic acid ester and other copolymerizable vinyl monomer, and exhibits a fluidity of not greater than 8 (MFR: measured under heating at 230° C. and compression at 37.3 N); and

thermoplastic acrylic polymer (B2):

being produced by copolymerizing a monomer component comprising not less than 92% by weight of a methacrylic acid ester and not greater than 8% by weight of at least one selected from an acrylic acid ester and other copolymerizable vinyl monomer, and exhibits a fluidity of not less than 15 (MFR: measured under heating at 230° C. and compression at 37.3 N);

the film having a prism type retroreflection structure formed on the surface thereof.

10. An acrylic film, which was obtained from a composition comprising the following acrylic polymer (A) and the following thermoplastic acrylic polymer (B3), and

the gel content being 25 to 50% by weight with respect to 100% by weight in total of the acrylic polymer (A) and the thermoplastic acrylic polymer (B3),

acrylic polymer (A):

being produced by polymerizing a monomer component (a-2) comprising not less than 80% by weight of a methacrylic acid ester and 20 to 0% by weight of an acrylic acid ester, in the presence of a crosslinked acrylic polymer (A-1),

having a graft rate of the monomer component (a-2) to the crosslinked acrylic polymer (A-1) being 50 to 140% by weight,

being in a particulate form having a weight average particle diameter of 300 to 3,000 Å, and

having a reduced viscosity (as measured with a 0.3% solution in N,N′-dimethylformamide at 30° C.) of methyl ethyl ketone (MEK) soluble-matter being not greater than 0.35 dl/g,

wherein, the crosslinked acrylic polymer (A-1) is produced by copolymerizing a monomer component (a-1) comprising 100 parts by weight of an acrylic monomer and 0.2 to 2 parts by weight of a polyfunctional monomer having two or more nonconjugated double bonds per molecule and being capable of copolymerizing with the acrylic monomer, and has a single-layer or multilayer structure, with each layer constituting the crosslinked acrylic polymer (A-1) having a glass transition temperature of less than 0° C.; and

thermoplastic acrylic polymer (B3):

being produced by copolymerizing a monomer component comprising not less than 80% by weight of a methacrylic acid ester, and 0 to 20% by weight of at least one selected from an acrylic acid ester and other copolymerizable vinyl monomer, and has a reduced viscosity of not greater than 0.35 dl/g (as measured with a 0.3% solution in N,N′-dimethylformamide at 30° C.);

the film having a prism type retroreflection structure formed on the surface thereof.

11. The acrylic film according to claim 1 , wherein the composition further comprises a colorant.

12. The acrylic film according to claim 1 , which has a thickness of 10 to 500 μm.

13. A retroreflection sheet constituted with the acrylic film according to claim 1 .

14. A retroreflection sheet constituted with the acrylic film according to claim 1 , and a surface protective film laminated on the acrylic film on the surface on which the prism type retroreflection structure was not formed.

15. The acrylic film according to claim 1 , wherein the acrylic film has a prism type retroreflection structure formed on the surface thereof by thermal transfer.

16. A process for producing the acrylic film according to claim 1 , comprising:

molding a flat film from the composition, and then

thermal transferring a prism type retroreflection structure on one surface of the flat film using a die.

17. The acrylic film according to claim 1 , which exhibits a retroreflection coefficient of not less than 200.