Green cement for sustainable construction
View Patent ↗“Green” cements, which can be carbon neutral or negative, can be prepared at lower temperatures (450° C.-500° C.) by utilizing feed compositions comprising (i) TiO 2 , TaO x N y , TiO x N y , RuO 2 , Pt, TaO, band gap materials, or a first mixture thereof; (ii) Al 2 O 3 ; and (iii) Ca 2 SiO 4 , MgSiO 2 , MnSiO 2 , or a second mixture thereof; and spent wash with melanoidin as a binder.
1. A particulate feed composition for preparing cement clinker comprising
(i) TiO 2 , TaO x N y , TiO x N y , RuO 2 , Pt, TaO, band gap materials, or a first mixture thereof;
(ii) Al 2 O 3 ; and
(iii) Ca 2 SiO 4 , MgSiO 2 , MnSiO 2 , or a second mixture thereof;
wherein (i), (ii), and (iii) are present in the particulate feed composition in a weight ratio of about 1:4:5, respectively.
2. The particulate feed composition of claim 1 , further comprising a spent wash.
3. The particulate feed composition of claim 2 , wherein the spent wash comprises melanoidin.
4. The particulate feed composition of claim 2 , wherein the spent wash comprises a distillery spent wash and/or spent wash from the processing of sugar.
5. The particulate feed composition of claim 2 , wherein the feed composition comprises about 95 wt % to about 98 wt % of (i), (ii), and (iii) combined, and about 2 wt % to about 5 wt % of the spent wash.
6. The particulate feed composition of claim 1 , wherein less than about 15 wt % of the particulate feed composition has a diameter greater than about 90 μm.
7. A cement clinker comprising about 40 wt % Al 2 O 3 , about 30 wt % SiO 2 , about 10 wt % TiO 2 and about 20 wt % spent wash.
8. A method for producing a cement clinker comprising,
providing a particulate feed composition of claim 1 to a cement kiln;
and heating the cement kiln to a temperature between about 450° C. and about 550° C. for a period of time suitable to form the cement clinker.
9. The method of claim 8 , wherein the heating is for about 5 to about 6 hours.
10. A cement clinker prepared according to the method of claim 8 .
11. The cement clinker of claim 7 , wherein the clinker has a pore size of about 100 nm to about 500 nm.
12. A method for producing a cement comprising,
providing a particulate feed composition of claim 1 to a cement kiln;
heating the cement kiln to a temperature between about 450° C. and about 550° C. for a period of time suitable for the formation of a cement clinker;
cooling the cement clinker; and
grinding the cement clinker with one or more additional materials to form the cement,
wherein the one or more additional materials comprises gypsum, fly ash, blast furnace slag, volcanic ash, silica fume, or a mixture thereof.
13. The method of claim 12 , wherein the heating is for about 5 to about 6 hours.
14. The method of claim 12 , wherein less than about 5 wt % of the cement has a particle diameter greater than about 45 μm.
15. The method of claim 14 , wherein less than about 15 wt % of the cement has a particle diameter less than 5 μm.
16. The method of claim 12 , wherein the cement has a pore size of about 100 nm to about 500 nm.
17. A cement prepared according to claim 12 .
18. A cement comprising the cement clinker of claim 7 .
19. A concrete comprising the cement of claim 17 and an aggregate.