Nanostructured hydroxyapatite coating for dental and orthopedic implants
View Patent ↗A high-strength coating for dental and orthopedic implants utilizing hydroxyapatite (HAp) nanoparticles provides for a high level of osseointegration through a range of surface pore sizes in the micro- to nanoscale. Zinc oxide (ZnO) nanoparticles may be incorporated with the HAp nanoparticles to form a composite coating material, with ZnO providing infection resistance due to its inherent antimicrobial properties. A textured surface, consisting of “islands” of roughly square coating structures measuring about 250 μm on a side, with spacing of 50-100 μm therebetween, may further promote the osseointegration and antimicrobial properties of the implant coating.
1. A medical implant comprising a substrate and a coating material deposited directly onto the substrate,
wherein the coating material comprises a sintered homogenous mixture of HAp nanoparticles with a grain size of about 50 nm to about 300 nm consisting essentially of HAp and ZnO particles consisting essentially of ZnO, and
wherein the coating material comprises an interconnected network of pores ranging from nano-scale pores to micro-scale pores extending along the x-, y-, and z-axes, and an array of projecting square-shaped microstructures that are about 250 μm on a side and with intersecting channel-shaped spaces therebetween having a width of about 50 to 100 μm.
2. The medical implant of claim 1 , further comprising a second coating material on top of the coating material.
3. The medical implant of claim 2 , wherein the second coating material comprises a material selected from the group consisting of HAp, ZnO, Ag, Au, and TiO 2 .
4. The medical implant of claim 1 , further comprising a therapeutic drug applied to the coating.
5. The medical implant of claim 1 , wherein the coating material comprises a surface texture.
6. The implant of claim 1 , wherein the coating material demonstrates a critical load of delamination of at least 10 N.
7. The implant of claim 1 , wherein the coating material comprising a surface area configured to bond to a plurality of cell tissues along at least 85% of the surface area.
8. A method for manufacturing the medical implant of claim 1 comprising a substrate and a coating material deposited directly onto the substrate, wherein the coating comprises nano-sized HAp particles, the method comprising the steps of de-agglomerating the HAp particles; spraying the HAp particles from a spray gun onto the substrate to form the coating; and sintering the implant whereby the coating is bound to the substrate, wherein the resulting coating comprises a plurality of pores with dimensions in the range of nano-size to micro-size.
9. The method of claim 8 , wherein the sintering step comprises microwave sintering.
10. The method of claim 8 , wherein the de-agglomerating step comprises the step of ball milling.
11. The method of claim 8 , wherein the de-agglomerating step comprises the step of jet milling.
12. The method of claim 11 , wherein the de-agglomerating step further comprises the step of ball milling.
13. The method of claim 8 , wherein a mask is introduced between the spray gun and the substrate before the electrostatically spraying step.
14. The method of claim 8 , wherein the HAp particles comprise a dimension in the range of about 50 nm to about 300 nm.
15. The method of claim 8 , wherein the resulting coating comprises a textured surface.
16. The method of claim 8 , wherein the coating comprises a plurality of islands of nano-sized particles.
17. The method of claim 16 , wherein the islands comprise a side length of about 250 μm.
18. The method of claim 17 , wherein a distance between the islands is in the range of about 50 μm to about 100 μm.
19. The method of claim 8 , wherein the pores range in dimension from less than 100 nm to more than 1 μm.
20. The method of claim 8 , further comprising a step of infiltrating the coating with a compound that can be leached when the implant is implanted in to a living organism.
21. The method of claim 8 , wherein said spraying step is performed by means of a spraying method selected from the group consisting of ESC, an ESC hybrid method, and an ESC spin-off method.