Toughened polyhydroxyalkanoate compositions

1. A method of forming a biodegradable polymeric composition, comprising combining:

a) a biologically-produced polyhydroxyalkanoate polymer;

b) a toughening composition that includes a vinyl acetate polymer, the vinyl acetate polymer having from 60 percent to 100 percent by weight of vinyl acetate monomer, the remainder of monomers being selected from at least one of the following:

(i) up to about 14 weight percent ethylene;

(ii) (meth)acrylic esters;

(iii) vinyl esters having from 1 to 12 carbon atoms in the carboxylic acid radical, provided that the vinyl ester is not vinyl acetate;

(iv) a carboxyl-group-containing monomer selected from the group consisting of acrylic acid, methacrylic acid, crotonic acid, itaconic acid, fumaric acid, maleic acid, and salts thereof;

(v) glycidyl methacrylate, hydroxyethyl methacrylate, acrylamide and vinyl pyrrolidone; and

(vi) vinyl alcohol;

c) a nucleating agent; and

d) a peroxide branching agent,

thereby forming a biodegradable polymeric composition.

2. The method of claim 1 , wherein the vinyl acetate polymer is a vinyl acetate homopolymer.

3. The method of claim 1 , wherein the vinyl acetate polymer is a a vinyl acetate copolymer having from about 84 to about 99 percent by weight of vinyl acetate monomer and from about 1 to 16 percent by weight of ethylene and acrylate comonomers.

4. The method of claim 1 , wherein the vinyl acetate polymer is a vinyl acetate copolymer having up to about 15 percent by weight of a polyvinyl alcohol, said polyvinyl alcohol having from about 60 to about 99.8 percent by weight degree of hydrolysis.

5. The method of claim 1 , wherein the biologically-produced polyhydroxyalkanoate polymer is in the form of a fine particle size powder and the vinyl acetate polymer is in the form of an emulsion, and wherein combining is done in an aqueous process prior to thermally removing water.

6. The method of claim 1 , wherein the biodegradable polymeric composition comprises from 50 parts by weight to 90 parts by weight of the biologically-produced polyhydroxyalkanoate polymer, and from 10 parts by weight to 50 parts by weight of the toughening composition.

7. The method of claim 1 , wherein the biologically-produced polyhydroxyalkanoate polymer is a poly(3-hydroxybutyrate) homopolymer, a poly(3-hydroxybutyrate-co-4-hydroxybutyrate), a poly(3-hydroxybutyrate-co-3-hydroxyvalerate), a poly(3-hydroxybutyrate-co-5-hydroxyvalerate), or a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate).

8. The method of claim 1 , wherein the biologically-produced polyhydroxyalkanoate polymer is a poly(3-hydroxybutyrate) homopolymer, a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with 5% to 15% 4-hydroxybutyrate content, a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with 5% to 22% 3-hydroxyvalerate content, a poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with 5% to 15% 5-hydroxyvalerate content, or a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with 3% to 15% 3-hydroxyhexanoate content.

9. The method of claim 1 , wherein the biologically-produced polyhydroxyalkanoate is a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate); a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate); a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate); a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate); a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) or a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate).

10. The method of claim 1 , wherein the biologically-produced polyhydroxyalkanoate is a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 5% to 15% 4-hydroxybutyrate content; a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content; a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content; a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 5% to 15% 4-hydroxybutyrate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content; a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with 5% to 15% 4-hydroxybutyrate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content or a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content.

11. The method of claim 1 , wherein the biologically-produced polyhydroxyalkanoate is a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate) homopolymer blended to with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); or a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b).

12. The method of claim 11 , wherein the weight of polymer a) is 20% to 60% of the combined weight of polymer a) and polymer b) and the weight of polymer b) is 40% to 80% of the combined weight of polymer a) and polymer b).

13. The method of claim 1 , wherein the biologically-produced polyhydroxyalkanoate is a) poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 20-50% 4-hydroxybutyrate content; a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with a 20% to 50% 5-hydroxyvalerate content; a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) having a 5%-50% 3-hydroxyhexanoate content; a) poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 5% to 15% 4-hydroxybutyrate content blended with b) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 20-50% 4-hydroxybutyrate content; a) poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 5% to 15% 4-hydroxybutyrate content blended with b) a poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with a 20% to 50% 5-hydroxyvalerate content; a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with 5% to 15% 4-hydroxybutyrate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) having a 5%-50% 3-hydroxyhexanoate content; a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content blended with b) poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 20-50% 4-hydroxybutyrate content; a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content blended with b) a poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with a 20% to 50% 5-hydroxyvalerate content; a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) having a 5%-50% 3-hydroxyhexanoate content; a) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content blended with b) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 20-50% 4-hydroxybutyrate content; a) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content blended with b) a poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with a 20% to 50% 5-hydroxyvalerate; or a) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) having a 5%-50% 3-hydroxyhexanoate content.

14. The method of claim 1 , wherein the biologically-produced polyhydroxyalkanoate is a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 20-50% 4-hydroxybutyrate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 20% to 50% 5-hydroxyvalerate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) having a 5%-50% 3-hydroxyhexanoate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 5% to 15% 4-hydroxybutyrate content blended with b) poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 20-50% 4-hydroxybutyrate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 5% to 15% 4-hydroxybutyrate content blended with b) poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with a 20% to 50% 5-hydroxyvalerate and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 5% to 15% 4-hydroxybutyrate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) having a 5%-50% 3-hydroxyhexanoate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content blended with b) poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 20-50% 4-hydroxybutyrate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content blended with b) a poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with a 20% to 50% 5-hydroxyvalerate and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) having a 5%-50% 3-hydroxyhexanoate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content blended with b) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 20-50% 4-hydroxybutyrate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content blended with b) a poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with a 20% to 50% 5-hydroxyvalerate and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); or a) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) having a 5%-50% 3-hydroxyhexanoate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b).

15. The method of claim 14 , wherein the weight of polymer a) is 20% to 60% of the combined weight of polymer a) and polymer b) and the weight of polymer b) is 40% to 80% of the combined weight of polymer a) and polymer b).

16. The method of claim 1 , wherein the biologically-produced polyhydroxyalkanoate is further blended with polymer c) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 20% to 50% 4-hydroxybutyrate content; c) a poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with a 20% to 50% 5-hydroxyvalerate content, or c) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 5% to 50% 3-hydroxyhexanoate content.