POLYURETHANE FOAMING PROCESSES AND FOAM PROPERTIES USING HALOGENATED OLEFIN BLOWING AGENT
The present invention relates to a method of producing more uniformly distributed polyurethane form using blowing agents. More particularly, the present invention relates to a method of producing more uniformly distributed polyurethane foam for an application in which flow of liquid polyurethane foam prior to solidification is important to its performance using a hydrochlorofluoroolefin (HCFO), such as 1233zd.
1 . Polyurethane foam with density variation, which is defined by overall density minus core, from 0.10 to 0.65 pcf, preferably from 0.15 to 0.50 pcf.
2 . A method of producing polyurethane foam comprises (i) mixing blowing agent with other polyurethane premix components; (ii) high pressure mixing and dispensing equipment of reaction injection molding
3 . A polymer blowing agent composition for polyurethane foams comprising about 70 wt % or more trans stereoisomer of hydrochlorofluoroolefin. 1233zd.
4 . The polymer blowing agent composition of claim 3 wherein said hydrochlorofluoroolefin 1233zd comprises about 90 wt % or more trans stereoisomer.
5 . The polymer blowing agent composition of claim 3 wherein said hydrochlorofluoroolefin 1233zd comprises about 97 wt % or more trans stereoisomer.
6 . The polymer blowing agent composition of claim 3 , further comprising a hydroflouorocarbon.
7 . The polymer blowing agent composition of claim 6 wherein said hydrofluorocarbon is sleeted from the group consisting of difitioromethane (HFC32); 1,1,1,2,2-pentalluomethane (HFC125); 1,1,1-trifluoroethane (HFC143a); 1,1,2,2-tetrafluorothane (HFC 134); 1,1,1,2-tetrafluoroethane (HFC134a); 1,1-difluoroethane (HFC152a); 1,1,1,2,3,3,3-heptafluoropropane (HFC227ea); 1,1,1,3,3-pentafluopropane (HFC245fa.); 1,1,1,3,3-pentafluobutane (HFC365mfc) and 1,1,1,2,2,3,4,5,5,5-decafluoropentane (HFC4310mee).
8 . The polymer blowing agent composition of claim 3 , further comprising a hydrofluoroolefin.
9 . The polymer blowing agent composition of claim 8 wherein said hydrofluoroolefin is selected from the group consisting of tetrafluoropropenes (HFO1234); trifluoropropenes (HFO1243); tetrafluorobutene isomers (HFO1354); pentafluorobutene isomers (HFO1345); hexafluorobutene isomers (HFO1336); heptafluorobutene isomers (HFO1327); heptafluoropentene isomers (HFO1447); octafluoropentene isomers (HFO1438); nonafluoropentene isomers (HFO1429), C4F9OCH3 (HFE-7100), C4F9OC2H5 (HFE-7200), CF3CF2OCH3 (HFE-245ch2), CF3CH2CHF2 (HFE-245fa), CF3CH2OCF3 (HFE-236fa), C3F7OCH3 (HFE-7000), 2-trifluoromethyl-3-ethoxydodecofluorobexane (HFE 7500), 1,1,1,2,3-hexafluoro-4-(1,1,2,3,3,3-hexafluoropropoxy)-pentane (HFE-7600), 1,1,1,2,2,3,5,5,5-decafluoro-3-methoxy-4-(trifluoromethyl)pentane (HFE-7300), ethyl nonafluoroisobutyl ether/ethyl nonafluorobutyl ether (HFE 8200), CHF2OCHF2, CHF2-OCH2F, CH2F—OCH2F, CH2F—O—CH3, cyclo-CF2CH2CF2-O, cyclo-CF2CF2CH2-O, CHF2-CF2CHF2, CF3CF2-OCH2F, CHF2-O—CHFCF3, CHF2-OCF2CHF2, CH2F—O—CF2CHF2, CF3-O—CF2CH3, CHF2CHF—O—CHF2, CF3-O—CHFCH2F, CF3CHF—O—CH2F, CF3-O—CH2CHF2, CHF2-O—CH2CF3, CH2FCF2-O—CH2F, CHF2-O—CF2CH3, CHF2CF2-O—CH3 (HFE254 pc), CH2F—O—CHFCH2F, CHF2-CHF—O—CH2F, CF3-O—CHFCH3, CF3CHF—O—CH3, CHF2-O—CH2CHF2, CH3-O—CH2CH2F, CF3CH2-O—CH2F, CF2HCF2CF2-O—CH3, CF3CHFCF2-O—CH3, CHF2CF2CF2-O—CH3, CHF2CF2CH2-OCHF2, CF3CF2CH2-O—CH3, CHF2CF2-O—CH2CH3, (CF3)2CF—O—CH3, (CF3)2CH—O—CHF2, (CF3)2CH—O—CH3, and mixture thereof.
10 . The polymer blowing agent composition of claim 3 , further comprising an additive selected from the group consisting of hydrocarbons, C1 to C5 alcohols, C1 to C4 aldehydes, C1 to C4 ketones, C1 to C4 ethers, carbon dioxide, C1 to C4 diethers, and mixture thereof.
11 . The polymer blowing agent composition of claim 3 , further comprising a hydrofluoroether.
12 . The polyurethane foam of claim 1 , with density variation, which is defined by overall density minus core, from 0.15 to 0.50 pcf.
13 . The polyurethane foam of claim 1 with density variation, which is defined by overall density minus core, from 0.20 to 0.45 pcf.