UV curable inkjet compositions for high-density print heads

1. A combination of:

a) an inkjet print head having a nozzle density of at least 600 dpi and including nozzles with an outer nozzle diameter D smaller than 25 μm; and

b) a UV curable inkjet composition containing 0 to 10 wt % of one or more monofunctional monomers and at least A wt % of 2-(2-vinyloxyethoxy)ethyl acrylate, wherein both wt % are based on the total weight of the UV curable inkjet composition, and

A is defined by Formula (I):

100 wt %− D× 3.0 wt %/μm≦ A≦ 100 wt %− D× 1.0 wt %/μm  Formula (I).

2. The combination according to claim 1 , wherein A is defined by Formula (II):

100 wt %− D× 2.5 wt %/μm≦ A≦ 100 wt %− D× 1.5 wt %/μm  Formula (II).

3. The combination according to claim 1 , wherein the outer nozzle diameter D is between 14 and 22 μm.

4. The combination according to claim 1 , wherein the UV curable inkjet composition contains at least 10 wt % of a polyfunctional monomer based on the total weight of the UV curable inkjet composition.

5. The combination according to claim 4 , wherein the polyfunctional monomer is a polyfunctional acrylate having two or more acrylate groups.

6. The combination according to claim 1 , wherein the UV curable inkjet composition contains a colour pigment.

7. The combination according to claim 1 , wherein the UV curable inkjet composition includes polymerizable compounds that are all acrylates.

8. The combination according to claim 1 , wherein the UV curable inkjet composition contains 0 to 3 wt % of organic solvent.

9. A combination of:

a) an inkjet print head having a nozzle density of at least 600 dpi and including nozzles with an outer nozzle diameter D smaller than 25 μm; and

b) a UV curable inkjet composition containing 0 to 10 wt % of one or more monofunctional monomers and at least A wt % of 2-(2-vinyloxyethoxy)ethyl acrylate, wherein both wt % are based on the total weight of the UV curable inkjet composition, and

A is defined by Formula (I):

100 wt %− D× 3.0 wt %/μm≦ A≦ 100 wt %− D× 1.0 wt %/μm  Formula (I)

wherein the UV curable inkjet composition has a viscosity ≦8 mPa·s at 45° C. and at a shear rate of 1000 s −1 .

10. An inkjet printing system comprising:

the combination as defined by claim 1 ; and

a UV curing device or an e-beam curing device.

11. An inkjet printing method comprising the steps of:

a) providing an inkjet printer containing at least one inkjet print head having a nozzle density of at least 600 dpi and including nozzles with a diameter D smaller than 25 μm;

b) jetting, at a temperature between 30° C. and 50° C., a UV curable inkjet composition containing 0 to 10 wt % of one or more monofunctional monomers and at least A wt % of 2-(2-vinyloxyethoxy)ethyl acrylate, wherein both wt % are based on the total weight of the UV curable inkjet composition; and

A is defined by Formula (I):

100 wt %− D× 3.0 wt %/μm≦ A≦ 100 wt %− D× 1.0 wt %/μm  Formula (I);

c) curing the UV curable inkjet composition.

12. The inkjet printing method according to claim 11 , wherein the inkjet printer includes a plurality of the inkjet print heads having a nozzle density of at least 600 dpi and including nozzles with a diameter D smaller than 25 μm.

13. The inkjet printing method according to claim 11 , further comprising the step of:

printing using an UV curable inkjet ink set comprising a plurality of the UV curable inkjet compositions including at least one cyan UV curable inkjet ink, at least one magenta UV curable inkjet ink, at least one yellow UV curable inkjet ink, and at least one black UV curable inkjet ink.

14. The inkjet printing method according to claim 11 , wherein a droplet volume of the UV curable inkjet composition is smaller than 20 pL.

15. An inkjet printing method comprising the steps of:

a) providing an inkjet printer containing at least one inkjet print head having a nozzle density of at least 600 dpi and including nozzles with a diameter D smaller than 25 μm;

b) jetting, at a temperature between 30° C. and 50° C., a UV curable inkjet composition containing 0 to 10 wt % of one or more monofunctional monomers and at least A wt % of 2-(2-vinyloxyethoxy)ethyl acrylate, wherein both wt % are based on the total weight of the UV curable inkjet composition;

A is defined by Formula (I):

100 wt %− D× 3.0 wt %/μm≦ A≦ 100 wt %− D× 1.0 wt %/μm  Formula (I);

c) curing the UV curable inkjet composition; and

printing a complete image in a single pass of the inkjet printer.