Glossy recording medium for inkjet printing
View Patent ↗An inkjet recording medium and a coating composition for forming an inkjet recording medium. In accordance with one aspect of the present invention, an inkjet recording medium is disclosed comprising an inkjet-receptive coating on a paper substrate. The inkjet-receptive coating contains a synergistic combination of pigments, binder and a multivalent metal salt such that the inkjet recording medium exhibits improved inkjet print properties, particularly when printed with a high speed inkjet printer using pigmented inks.
1. A method of printing comprising:
providing an inkjet recording medium comprising:
a paper substrate; and
an inkjet-receptive coating comprising a primary pigment having an average particle size of less than 1 microns;
a secondary pigment having an average particle size of 3 to 5 microns;
a multivalent salt; and
a binder wherein said binder is compatible with the multivalent salt and present in an amount from about 2 to 15 parts by weight of based on 100 parts total pigments; and
applying an inkjet ink to said inkjet recording medium wherein said ink comprises an aqueous ink composition comprising a pigment-based colorant.
2. An inkjet recording medium comprising:
a paper substrate; and
an inkjet-receptive coating comprising a primary pigment having an average particle size of less than 1 microns;
a secondary pigment having an average particle size of 3 to 5 microns;
a multivalent salt;
a binder wherein said binder is compatible with the multivalent salt and present in an amount from about 2 to 15 parts by weight of based on 100 parts total pigments;
wherein said binder comprises a natural latex binder comprising starch nanoparticles having an average particle size of less than 400 nm; or
a biopolymer latex conjugate comprising a biopolymer-additive complex reacted with a crosslinking agent.
3. The inkjet recording medium of claim 2 wherein said binder comprises a stabilized anionic synthetic styrene butadiene latex binder.
4. The inkjet recording medium of claim 2 wherein the multivalent metal salt is selected from the group consisting of calcium chloride, calcium acetate, calcium nitrate, magnesium chloride, magnesium acetate, magnesium nitrate, magnesium sulfate, barium chloride, barium nitrate, zinc chloride, zinc nitrate, aluminum chloride, aluminum hydroxychloride, aluminum nitrate and mixtures thereof.
5. The inkjet recording medium of claim 4 wherein the multivalent metal salt comprises calcium chloride.
6. An inkjet recording medium comprising:
a paper substrate; and
an inkjet-receptive coating comprising a primary pigment having an average particle size of less than 1 microns;
a secondary pigment having an average particle size of 3 to 5 microns;
a multivalent salt;
a binder wherein said binder is compatible with the multivalent salt and present in an amount from about 2 to 15 parts by weight of based on 100 parts total pigments; and
a plastic pigment present in an amount of about 5 to 15 parts per 100 parts total pigments.
7. An inkjet recording medium comprising:
a paper substrate; and
an inkjet-receptive coating comprising a primary pigment having an average particle size of less than 1 microns;
a secondary pigment having an average particle size of 3 to 5 microns;
a multivalent salt;
a binder wherein said binder is compatible with the multivalent salt and present in an amount from about 2 to 15 parts by weight of based on 100 parts total pigments; and
a dispersant selected from the group consisting of dispersants containing polymers with pigment affinic groups, polyether polycarboxylate salts and polyoxyalkylene salts.
8. An inkjet recording medium comprising:
a paper substrate; and
an inkjet-receptive coating comprising a primary pigment having an average particle size of less than 1 microns;
a secondary pigment having an average particle size of 3 to 5 microns;
a multivalent salt;
a binder wherein said binder is compatible with the multivalent salt and present in an amount from about 2 to 15 parts by weight of based on 100 parts total pigments; and
wherein the inkjet recording medium has a TAPPI 75° gloss of about 25 to 40% or 55 to 75%.
9. The inkjet recording medium of claim 8 wherein each of said primary and secondary pigments comprises calcium carbonate.
10. The inkjet recording medium of claim 8 wherein said coating comprises a blend of a synthetic latex binder and a natural latex binder.
11. An inkjet-receptive coating composition comprising:
a primary pigment having an average particle size of less than 1 microns;
a secondary pigment having an average particle size of 3 to 5 microns;
a multivalent salt; and a binder wherein said binder is present in an amount from about 2 to 15 parts by weight of based on 100 parts total pigments; and
a dispersant selected from the group consisting of dispersants containing polymers with pigment affinic groups, polyether polycarboxylate salts and polyoxyalkylene salts.