Manufacturing method of making aluminum alloy semi-finished product with improved microporosity
View Patent ↗The invention relates to a manufacturing method for making an unwrought semi-finished product having at mid thickness a density of micropores of size greater than 90 μm less than 50% and preferably less than 20% of the density of micropores of size greater than 90 μm obtained by a method according to prior art. The method according to the invention comprises in particular an ultrasound treatment step for the molten metal bath in a furnace and/or a vessel using an immersed device comprising at least one ultrasound transmitter. The semi-finished products obtained according to the method of the invention are particularly advantageous for manufacturing by rolling sheets designed for the aircraft industry to produce spars, ribs, upper and lower wing skins and for manufacturing by extrusion sections designed for the aircraft industry to produce stiffeners.
1. A manufacturing method for an unwrought aluminum alloy semi-finished product optionally comprising a rolling slab and/or an extrusion billet, said method comprising:
(i) preparing a molten metal bath of an alloy having a composition comprising, percentage by weight:
Zn: 0-12
Cu: 0-6
Mg: 0-6
Li: 0-3
Ag: 0-1
Si<0.5
Fe<0.5
optionally at least one of Cr, Zr, Mn, Hf, Ti, Sc, V, B, with a content <0.5,
remainder aluminum,
(ii) treating with ultrasound said molten metal bath in a furnace and/or a vessel using an immersed device comprising at least one ultrasound transmitter,
(iii) transferring said molten metal bath so treated to a solidification device,
(iv) vertical direct chill semi-continuous casting said treated molten metal bath,
wherein a duration elapsing between an end of said treating with ultrasound of the liquid metal bath and an introduction of said liquid metal bath in the solidification device is at least a few minutes and optionally comprises at least three minutes.
2. A manufacturing method for an unwrought aluminum alloy semi-finished product optionally comprising a rolling slab and/or an extrusion billet, said method comprising:
(i) preparing a molten metal bath of an alloy having a composition comprising, percentage by weight:
Zn: 0-12
Cu: 0-6
Mg: 0-6
Li: 0-3
Ag: 0-1
Si<0.5
Fe<0.5
optionally at least one of Cr, Zr, Mn, Hf, Ti, Sc, V, B, with a content <0.5,
remainder aluminum,
(ii) treating with ultrasound said molten metal bath in a furnace and/or a vessel using an immersed device comprising at least one ultrasound transmitter,
(iii) transferring said molten metal bath so treated to a solidification device,
(iv) vertical direct chill semi-continuous casting said treated molten metal bath,
wherein a semi-finished product obtained by said method has at mid thickness, a density of micropores of a size greater than 90 μm, that is less than 50% of a density of micropores of a size greater than 90 μm obtained by a method that is identical to said method but does not includes said treating by ultrasound.
3. A method of claim 2 , wherein a semi-finished product obtained by said method has at mid thickness, a density of micropores of a size greater than 90 μm, that is less than 20% of a density of micropores of a size greater than 90 μm obtained by a method that is identical said method but does not include said treating by ultrasound.