Method of purifying carbon nanotubes and applications thereof
View Patent ↗The present invention relates to a method of preparing purified carbon nanotubes (CNTs) comprising mixing starting CNTs with an organic solvent in the presence of sonication; substantially removing the organic solvent to obtain a CNT composition; and heating the CNT composition at 200° C. or higher to obtain the purified carbon nanotubes. The present invention further relates to the purified CNTs and cohesive CNT assemblies prepared from the method described herein, and articles (e.g. capacitor, energy storage device or capacitive deionization device) comprising the purified CNTs.
1. A method of preparing purified carbon nanotubes, comprising the steps of:
(a) obtaining starting carbon nanotubes having carbonaceous impurities;
(b) mixing the starting carbon nanotubes with an organic solvent in the presence of sonication;
(c) substantially removing the organic solvent to obtain a carbon nanotube composition; and
(d) heating the carbon nanotube composition at 400-1100° C. in an atmosphere comprising between about 1 ppm to 10,000 ppm of oxygen to remove carbonaceous impurities without degrading or damaging the carbon nanotubes;
wherein the organic solvent is selected from the group consisting of toluene, o-dichlorobenzene, isopropyl alcohol, N,N-dimethylformamide, substituted or unsubstituted benzene, chlorobenzene, m-dichlorobenzene, p-dichlorobenzene, trichlorobenzene, bromobenzene, m-dibromobenzene, o-dibromobenzene, p-dibromobenzene, tribromobenzene, toluene, o-xylene, m-xylene, p-xylene, 1,2-dichloroethane, 1,2-dibromoethane, chloroform, primary amines, secondary amines, tertiary amines, dimethyl sulfoxide, and any combinations thereof.
2. The method according to claim 1 , further comprising mixing the starting carbon nanotubes and the solvent by a mechanical agitation method before, during, and/or after step (b), and before step (c).
3. The method according to claim 2 , wherein the mechanical agitation is mechanical stirring, high-shear mixing, or microfluidization.
4. The method according to claim 3 , wherein the mechanical agitation is high-shear mixing and is conducted during step (b).
5. The method according to claim 1 , wherein the solvent is toluene, isopropyl alcohol, N,N-dimethylformamide, o-dichlorobenzene, or any combination thereof.
6. The method according to claim 5 , wherein the solvent is toluene.
7. The method according to claim 5 , wherein the ratio of the starting carbon nanotubes and the solvent is between 0.01 and 100 mg per ml.
8. The method according to claim 5 , wherein step (b) provides a dispersion of carbon nanotubes in the solvent.
9. The method according to claim 1 , wherein in step (c), the solvent is removed by heating the carbon nanotube composition at a temperature between 20° C. and 200° C.
10. The method according to claim 1 , wherein in step (c), the solvent is removed in a substantially controlled manner to obtain the purified carbon nanotubes in the form of a cohesive carbon nanotube assembly.
11. The method according to claim 1 , wherein step (d) is performed for a time period between about 30 minutes and about 30 hours.
12. The method according to claim 1 , wherein step (d) is performed at a temperature of 600-900° C.
13. The method according to claim 1 , wherein step (d) is performed in an atmosphere in which the non-oxygen content comprises at least 99% argon, helium, nitrogen, or any combination thereof.
14. The method according to claim 13 , wherein step (d) is performed at about 750° C. for about 12 hours in an atmosphere comprising at least 99% argon and between 20 and 2000 ppm oxygen.
15. A method of preparing purified carbon nanotubes having high specific surface area, comprising the steps of:
(a) obtaining starting carbon nanotubes;
(b) mixing the starting carbon nanotubes with an organic solvent comprising toluene, using high shear mixing, in the presence of sonication, to produce a dispersion;
(c) substantially removing the organic solvent by evaporation to obtain a carbon nanotube composition; and
(d) heating the carbon nanotube composition at a temperature of 200-1100° C. in an atmosphere comprising about 1-10,000 ppm oxygen.
16. The method according to claim 15 , wherein step (b) is performed for between about 20 minutes and about 8 hours.
17. The method according to claim 16 , wherein step (b) comprises a period of concurrent high-shear mixing and sonication performed for between about 10 minutes and about 2 hours, and a period of sonication with or without concurrent high-shear mixing performed for between about 10 minutes and about 6 hours.
18. The method according to claim 17 , wherein step (d) is performed at 600-900° C. in an atmosphere comprising at least 99% argon and about 20 to 2000 ppm oxygen.
19. The method according to claim 15 , wherein in step (c), the solvent is removed in a substantially controlled manner to obtain the purified carbon nanotubes in the form of a cohesive carbon nanotube assembly.