A magnet member excellent in both corrosion resistance and adhesion is provided. The magnet member 30 in accordance with the present invention is a magnet member comprising a magnet base body 32 including a rare-earth magnet and a plating film 34 containing Ni and covering the magnet base body 32 , while the plating film 34 has a sulfur content lower in a marginal part 38 in a surface S of the magnet base body having an easy magnetization direction M of the magnet base body 32 as a perpendicular thereto than in a center part 36 of the surface S.
1. A magnet member comprising:
a magnet base body including a rare-earth magnet; and
a plating film containing Ni that covers the magnet base body and forms an outermost layer of the magnet member, the plating film containing Ni comprising (i) a center part that coincides with a center of the magnet base body, and (ii) a marginal part;
wherein the plating film containing Ni has a sulfur content lower in the marginal part of the outermost layer of the magnet member than in the center part of the outermost layer of the magnet member,
wherein a surface of the plating film containing Ni that forms the outermost layer of the magnet member is perpendicular to an easy magnetization direction of the magnet base body, and
wherein the center part of the plating film containing Ni is surrounded by the marginal part of the plating film containing Ni, the center part having a 50% reduction ratio relative to the marginal part, wherein the plating film containing Ni is thicker in the marginal part than in the center part.
2. A magnet member according to claim 1 , wherein the sulfur content in the plating film in the marginal part is 0.80 to 0.95 times that in the center part.
3. A magnet member according to claim 1 , wherein the plating film containing Ni is formed by electroplating.
4. A magnet member according to claim 2 , wherein the plating film containing Ni is formed by electroplating.
5. A magnet member according to claim 1 , wherein the plating film containing Ni that forms the outermost layer of the magnet member comprises an outermost surface having a concave form.