View Patent ↗A coated article includes a substrate and a first coating formed over at least a portion of the substrate. The first coating includes a mixture of oxides including oxides of at least two of P, Si, Ti, Al and Zr. A photoactive functional coating is formed over at least a portion of the first coating. In one embodiment, the functional coating includes titania.
1. A method of increasing the photocatalytic activity of a photocatalytic coating, comprising the steps of:
forming a first coating over at least a portion of a substrate, the first coating comprising a mixture of phosphorous oxide and at least two other oxides selected from the group consisting of oxides of Si, Ti, Al and Zr; and
forming a photocatalytic coating comprising crystalline titania over at least a portion of the first coating, wherein the crystalline titania has a thickness greater than 50 nm.
2. The method of claim 1 , wherein the first coating comprises oxides of Ti, Si and P.
3. The method of claim 1 , wherein the first coating comprises 30-80 volume % silica, 1-15 volume % phosphorus oxide, and 5-69 volume % titania and has a thickness in the range of 10 nm to 120 nm.
4. The method of claim 1 , wherein the first coating is a gradient coating.
5. The method of claim 1 , wherein the first coating is a multi-layer coating with each layer comprising phosphorous oxide, silica, and titania.
6. The method of claim 5 , wherein the first coating comprises a first layer, a second layer over the first layer, and a third layer over the second layer, and wherein a volume % of silica in the second layer is less than a volume % of silica in the first or third layers.
7. The method of claim 1 , wherein the first coating is a multi-layer coating comprising:
a first layer comprising 5-10 volume % phosphorous oxide, 70-80 volume % silica and 10-25 volume % titania with a thickness in the range of 11 nm to 29 nm;
a second layer comprising 2 volume % phosphorous oxide, 48-62 volume % silica and 36-50 volume % titania with a thickness in the range of 21 nm to 33 nm; and
a third layer comprising 5-11 volume % phosphorous oxide, 70-80 volume % silica and 9-25 volume % titania with a thickness in the range of 15 nm to 23 nm.
8. The method of claim 1 , wherein at least one of the first and second coatings is deposited by CVD.
9. The method of claim 1 , wherein the photoactive coating comprises anatase crystalline titania.
10. A method of increasing the photocatalytic activity of a photocatalytic coating, comprising the steps of:
forming a first coating over at least a portion of a substrate, the first coating comprising a mixture of phosphorus oxide and at least two other oxides selected from the group consisting of oxides of Si, Ti, Al and Zr; and
forming a photocatalytic coating comprising anatase crystalline titania over at least a portion of the first coating, wherein the crystalline titania has a thickness greater than 50 nm,
wherein the first coating is a multi-layer coating comprising:
a first layer comprising phosphorous oxide, silica, and titania, with the silica present in the range of 70-80 volume %;
a second layer comprising phosphorous oxide, silica, and titania, with the silica present in the range of 48-62 volume %; and
a third layer comprising phosphorous oxide, silica, and titania, with the silica present in the range of 70-80 volume %.
11. The method of claim 1 , wherein the crystalline titania has a thickness greater than 100 nm.
12. The method of claim 10 , wherein the crystalline titania has a thickness greater than 100 nm.