Method for producing carbonitrided member
View Patent ↗A method for producing a carbonitrided member comprising the steps of carburizing a steel part having a composition of, by mass percent, C: 0.10 to 0.35%, Si: 0.15 to 1.0%, Mn: 0.30 to 1.0%, Cr: 0.40 to 2.0%, S: 0.05% or less with the balance being Fe and impurities in a carburizing atmosphere of 900 to 950° C. The carburized steel part is carbonitrided in a carbonitriding atmosphere with the temperature of 800 to 900° C. and the nitrogen potential of 0.2 to 0.6%. The carbonitrided steel part is qhenched and then shot peened. The shot peening treatment may be further performed while heating to a temperature not higher than 350° C. or immediately after heating to a temperature not higher than 350° C. After quenching, the shot peening treatment may be further performed after tempering in the temperature range exceeding 250° C. and not higher than 350° C.
1. A method for producing a carbonitrided member comprising the steps of:
carburizing a steel part having a composition of, by mass percent, C: 0.10 to 0.35%, Si: 0.15 to 1.0%, Mn: 0.30 to 1.0%, Cr: 0.40 to 2.0%, S: 0.05% or less with the balance being Fe and impurities in a carburizing atmosphere at a temperature of 900 to 950° C.;
then, while maintaining the carburizing atmosphere, carbonitriding the steel part immediately following the carburizing by holding the carburized steel part in a temperature of 800 -900C. in a carbonitriding atmosphere having a nitrogen potential of 0.2 to 0.6%;
quenching the carbonitrided steel part; and
shot peening the quenched steel part while heating to a temperature not higher than 350° C. or immediately after heating to a temperature not higher than 350° C., wherein the carburizing atmosphere is maintained with a constant carbon potential throughout carburizing and carbonitriding and up to quenching.
2. A method for producing a carbonitrided member comprising the steps of:
carburizing a steel part having a composition of, by mass percent, C: 0.10 to 0.35%, Si: 0.15 to 1.0%, Mn: 0.30 to 1.0%, Cr: 0.40 to 2.0%, S: 0.05% or less with the balance being Fe and impurities in a carburizing atmosphere at a temperature of 900 to 950° C.,
then, while maintaining the carburizing atmosphere, carbonitriding the steel part immediately following the carburizing by holding the carburized steel part at a temperature of 800-900 C in a carbonitriding atmosphere having a nitrogen potential of 0.2 to 0.6%;
quenching the carbonitrided steel part; and
tempering the quenched steel part in the temperature range exceeding 250° C. and not higher than 350° C. and then shot peening the tempered steel part, wherein the carburizing atmosphere is maintained with a constant carbon potential throughout carburizing and carbonitriding and up to quenching.
3. The method for producing a carbonitrided member according to claim 1 , wherein the composition of the steel part further contains Mo: 0.50% or less by mass percent in lieu of a part of Fe.
4. The method for producing a carbonitrided member according to claim 2 , wherein the composition of the steel part further contains Mo: 0.50% or less by mass percent in lieu of a part of Fe.