Nano-YAG:Ce phosphor compositions and their methods of preparation
View Patent ↗Disclosed herein are cerium doped, garnet phosphors emitting in the yellow region of the spectrum, and having the general formula (Y,A) 3 (Al,B) 5 (O,C) 12 :Ce 3+ , where A is Tb, Gd, Sm, La, Sr, Ba, Ca, and/or Mg, and substitutes for Y, B is Si, Ge, B, P, and/or Ga, and substitutes for Al, and C is F, Cl, N, and/or S, where C substitutes for O. Relative to a solid-state-reaction method, the instant co-precipitation methods provide a more homogeneous mixing environment to enhance the distribution of the Ce 3+ activator in the YAG matrix. Such a uniform distribution has the benefit of an increased emission intensity. The primary particle size of the as-prepared phosphor is about 200 nm, with a narrow distribution.
1. A cerium-doped, garnet-based phosphor comprising yttrium, aluminum, silicon, and oxygen, wherein the phosphor is configured to absorb excitation radiation having a peak wavelength ranging from about 445 nm to about 460 nm, and to emit light having a peak emission wavelength ranging from about 530 nm to about 550 nm, wherein the phosphor further includes a halogen.
2. The cerium-doped, garnet-based phosphor of claim 1 , wherein the phosphor is doped with about 3% silicon.
3. The cerium-doped, garnet-based phosphor of claim 1 , wherein the phosphor is doped with about 5% silicon.
4. The cerium-doped, garnet-based phosphor of claim 1 , wherein the phosphor is doped with about 8% silicon.
5. The cerium-doped, garnet-based phosphor of claim 1 ,wherein the silicon substitutes for aluminum in the range from about 3% to about 8%.
6. A cerium-doped, garnet-based phosphor comprising a compound having the formula Y 3 (Al 1-x Si x ) 5 O 12 :Ce 3+ , where x ranges from about 0.03 to about 0.08, and wherein the phosphor is configured to emit light having a peak emission wavelength ranging from about 530 nm to about 550 nm, and wherein the phosphor further includes a halogen.
7. A cerium-doped, garnet-based phosphor comprising a compound having the formula Y 3 (Al 1-x Si x ) 5 (O 1-y C y ) 12 :Ce 3+ , where
C is at least one of F or Cl;
x ranges from about 0.001 to about 0.2;
y ranges from about 0.001 to 0.2; and
wherein the phosphor is configured to emit light having a peak emission wavelength ranging from about 540 nm to about 560 nm.
8. The cerium-doped, garnet-based phosphor of claim 7 , wherein C is F.
9. A method of producing a phosphor having the formula Y 3 (Al 1-x Si x ) 5 O 12 :Ce 3+ , where x ranges from about 0.001 to about 0.2, and where the method comprises:
1) dissolving desired amounts of Ce(NO 3 ) 3 •6H 2 O, Y(NO 3 ) 3 •6H 2 O, Al(NO 3 ) 3 •9H 2 O in de-ionized water to form a solution and adding a halogen containing compound to the solution;
2) adding (CH 3 O) 4 Si to the solution resulting from step 1);
3) adding the solution from step 2) to an ammonia solution in a dropwise manner;
4) aging the solution of step 3) for about 1 hour, and then filtering and washing the resultant precipitant with distilled water;
5) drying the precipitate of step 4) at about 150° C. for about 6 hours; and
6) cooling and gently milling the dried precipitate of step 4), transferring this product to an alumina crucible, and sintering the milled product at about 1100° C. to 1500° C. in a reducing atmosphere.
10. A cerium-doped, garnet-based phosphor comprising a compound having the formula (Y,A) 3 (Al 1-x Ga x ) 5 (O,C) 12 :Ce 3+ , where x ranges from about 0.001 to 1.0, A is selected from the group consisting of Tb, Gd, Sm, La, Sr, Ba and Ca where A substitutes for Y in amounts ranging from about 0.1 to 100 percent, C is selected from the group consisting of F, Cl, N and S where C substitutes for O in amounts ranging from about 0.1 to 100 percent, and wherein the phosphor includes a halogen.
11. The cerium-doped, garnet-based phosphor of claim 10 , wherein the phosphor further includes silicon.
12. A cerium-doped, garnet-based phosphor comprising yttrium, aluminum, fluorine, and oxygen, wherein the phosphor is configured to absorb excitation radiation having a peak wavelength ranging from about 445 nm to about 460 nm, and wherein the peak emission wavelength is blue-shifted about 25 nm with the inclusion of 8% fluorine relative to no fluorine.
13. A cerium-doped, garnet-based phosphor comprising yttrium, aluminum, chlorine, and oxygen, wherein the phosphor is configured to absorb excitation radiation having a peak wavelength ranging from about 445 nm to about 460 nm, and wherein the peak emission wavelength is blue-shifted about 5 to 8 nm with the inclusion of 8% chlorine relative to no chlorine.