Black effect pigment
View Patent ↗This disclosure is directed to a black effect pigment and a method of forming said pigment. The pigment comprises a platy substrate coated with SnO 2 and/or SnO 2 hydrates and Fe 3 O 4 with an optional coating of metal oxides such as SiO 2 , TiO 2 , ZrO 2 and ZnO 2 . The deposition of the SnO 2 and/or SnO 2 hydrates onto the substrate improves the adhesion and prepares the substrate surface for deposition of the iron oxides onto the platy surface, especially mica surfaces. While the pigment may be used in such applications as coating, powder coating, printing ink, plastic, ceramic material, glass, cosmetic formulation, laser marking pigment, pigment composition or dry preparation, the pigment is especially suitable for cosmetic applications.
1. A black effect pigment comprising
a) at least a partial layer of SnO 2 and/or hydrated SnO 2 on a substrate,
b) at least a partial layer of Fe 3 O 4 , and
c) optionally, a further layer of metal oxide,
wherein the at least partial layer of Fe 3 O 4 may further contain ferric hydroxide and Fe 2 O 3 , and the SnO 2 and/or SnO 2 hydrate ranges from 0.5 to 4 wt. % and the Fe 3 O 4 ranges from 18.4 to about 70 wt % and the wt. % is based on the total weight of the black effect pigment.
2. The black effect pigment of claim 1 , wherein the SnO 2 and/or hydrated SnO 2 layer and/or the Fe 3 O 4 layer encapsulates or forms a continuous coating or layer on the substrate.
3. The pigment of claim 1 , which further layer c) is selected from the metal oxide group consisting of SiO 2 , TiO 2 , ZrO 2 , Al 2 O 3 and ZnO.
4. The pigment of claim 3 , wherein the metal oxide is SiO 2 or TiO 2 .
5. The pigment of claim 1 , wherein the pigment contains a metal oxide layer c) and the metal oxide layer is transparent.
6. The pigment of claim 1 , wherein the substrate is selected from the group consisting of aluminum oxide, platy glass, perlite, aluminum, natural mica, synthetic mica, bismuth oxychloride, platy iron oxide, platy graphite, bronze, stainless steel, natural pearl, boron nitride, silicon dioxide, copper flake, copper alloy flake, zinc flake, zinc alloy flake, zinc oxide, enamel, china clay, porcelain, titanium oxide, titanium dioxide, titanium suboxides, zeolite, kaolin, zeolites and combinations thereof.
7. The pigment of claim 1 , wherein the substrate is selected from the group consisting of natural mica, synthetic mica, perlite, platy glass and aluminum.
8. The pigment of claim 1 , with the proviso that the SnO 2 and/or SnO 2 hydrate coating or layer is not incorporated into a TiO 2 coating or layer.
9. The pigment of claim 1 , wherein the substrate is mica or synthetic mica.
10. The pigment of claim 1 , wherein the SnO 2 and Fe 3 O 4 are present in the same layer.
11. The pigment of claim 1 , wherein the SnO 2 and Fe 3 O 4 are present in two separate layers.
12. The pigment of claim 1 , which has the following layer structure:
substrate/SnO 2 and/or SnO 2 hydrate+Fe 3 O 4 (in same layer)
substrate/SnO 2 and/or SnO 2 hydrate+Fe 3 O 4 (in same layer)/SiO 2
substrate/SnO 2 and/or SnO 2 hydrate/Fe 3 O 4
substrate/SnO 2 and/or SnO 2 hydrate/Fe 3 O 4 /SiO 2
substrate/SnO 2 and/or SnO 2 hydrate/Fe 3 O 4 /TiO 2
substrate/SnO 2 and/or SnO 2 hydrate/Fe 3 O 4 /ZnO 2
substrate/SnO 2 and/or SnO 2 hydrate/Fe 3 O 4 /ZrO 2
substrate/TiO 2 +SnO 2 /Fe 3 O 4 /SiO 2
substrate/SnO 2 and/or SnO 2 hydrate/TiO 2 +SnO 2 /Fe 3 O 4 /SiO 2
substrate/TiO 2 +SnO 2 /SnO 2 and/or SnO 2 hydrate/Fe 3 O 4 /SiO 2
substrate/SnO 2 and/or SnO 2 hydrate/Fe 3 O 4 /TiO 2 +SnO 2 /Fe 3 O 4 /SiO 2
substrate/SnO 2 and/or SnO2 hydrate/Fe 3 O 4 /SiO 2 /SnO 2 /Fe 3 O 4 /SiO 2
substrate/SiO 2 /SnO 2 and/or SnO 2 hydrate/Fe 3 O 4 /TiO 2 , or
substrate/SnO 2 /TiO 2 /SnO 2 /Fe 3 O 4 /SiO 2 ,
wherein the substrate is selected from the group consisting of aluminum oxide, platy glass, perlite, aluminum, natural mica, synthetic mica, bismuth oxychloride, platy iron oxide, platy graphite, bronze, stainless steel, natural pearl, boron nitride, silicon dioxide, copper flake, copper alloy flake, zinc flake, zinc alloy flake, zinc oxide, enamel, china clay, porcelain, titanium oxide, titanium dioxide, titanium suboxide, zeolite, kaolin, borosilicate and combinations thereof.
13. A paint, coating, powder coating, printing ink, laser marking pigment, cosmetic formulation, pigment composition or dry preparation comprising the black effect pigment according to claim 1 .
14. A cosmetic formulation comprising the black effect pigment according to claim 1 .
15. The cosmetic formulation according to claim 14 , which further contains from about 10 to about 90 wt. % a cosmetically suitable carrier material.
16. The cosmetic formulation according to claim 14 , wherein the formulation is a cosmetic product selected from concealing sticks, foundations, stage make-up, mascaras, cake mascaras, cream mascaras, eye shadows, liquid eye shadows, pomade eye shadows, powder eye shadows, stick eye shadows, pressed eye shadows, cream eye shadows, hair color, lipsticks, lip gloss, kohl pencils, eye liners, blushers, eyebrow pencils, cream powders, nail enamels, skin glosser stick, hair sprays, face powders, leg-makeup, insect repellent lotion, nail enamel remover, perfume lotion, shampoos, gel shampoos, liquid shampoos, shaving creams, aerosol shaving creams, brushless shaving creams, lathering shaving creams, hair grooming products, cologne sticks, colognes, cologne emollients, bubble baths, body lotions, moisturizing body lotions, cleansing body lotions, analgesic body lotions, astringent body lotions, after shave lotions, after bath milks and sunscreen lotions.
17. A method of preparing the black effect pigment according to claim 1 , comprising the steps of
applying a coating or layer of Fe 3 O 4 which may further include ferric hydroxide or ferric oxide, onto an at least partially coated or layered SnO 2 which may further include hydrated SnO 2 coated substrate and optionally applying a further metal oxide coating.
18. The method according to claim 17 , wherein the substrate is selected from the group consisting of aluminum oxide, platy glass, perlite, aluminum, natural mica, synthetic mica, bismuth oxychloride, platy iron oxide, platy graphite, platy silica, bronze, stainless steel, natural pearl, boron nitride, copper flake, copper alloy flake, zinc flake, zinc alloy flake, zinc oxide, enamel, china clay, porcelain, titanium oxide, titanium dioxide, titanium suboxides, zeolites, kaolin and combinations thereof.
19. A method of increasing the adhesion of Fe 3 O 4 to a substrate comprising
the steps of a) at least partially coating the substrate with from 0.5 to 4 wt. %
SnO 2 or hydrated SnO 2 ,
b) applying from 18.4 to about 70 wt % of
Fe 3 O 4 to the at least partially coated substrate of step a)
and
c) optionally, applying a further metal oxide coating
and the wt. % is based on the total weight of the coated substrate.
20. The pigment of claim 1 , wherein the SnO 2 and/or SnO 2 hydrate partially or completely coats said substrate and is adjacently and directly coated with at least a partial coating or layer of Fe 3 O 4 .