NANOWIRE COATINGS, FILMS, AND ARTICLES
Coatings are disclosed comprising cellulosic polymers, silver nanowires, and surfactants that exhibit resistivities less than about 150 ohms per square and void densities less than about ⅜ voids per square inch. Such coatings and transparent films made from such coatings are useful in electronics applications.
1 . A coating comprising:
a first amount of at least one cellulosic polymer;
a second amount of silver nanowires, the ratio of the second amount to the first amount being between about 0.1 and about 1; and
a third amount of at least one surfactant comprising at least one of an anionic fluorosurfactant or a polymer comprising at least one fluorine atom, the ratio of the third amount to the first amount being between about 0.001 and about 1,
wherein the coating has a resistivity less than about 150 ohms per square and a void density less than about ⅜ voids per square inch.
2 . The coating according to claim 1 , wherein the at least one cellulosic polymer comprises at least one of a cellulose ester.
3 . The coating according to claim 1 , wherein the at least one cellulosic polymer comprises cellulose acetate butyrate.
4 . The coating according to claim 1 , wherein at least some of the silver nanowires have lengths greater than about 10 μm and diameters less than about 140 nm.
5 . The coating according to claim 1 , wherein at least some of the silver nanowires have lengths greater than about 10 μm and less than about 50 μm.
6 . The coating according to claim 1 , wherein the at least one surfactant comprises at least one of FLEXIPEL™ AM-101 partially fluorinated polymer, ZONYL® 9361 fluorosurfactant, CAPSTONE® FS-63 fluorosurfactant, or MASURF® FP-815CP anionic fluoroacrylate copolymer.
7 . The coating according to claim 1 , wherein the at least one surfactant comprises at least one of an anionic fluorosurfactant or a partially fluorinated copolymer.
8 . The coating according to claim 1 , wherein the at least one surfactant comprises at least one of FLEXIPEL™ AM-101 partially fluorinated polymer, ZONYL® 9361 fluorosurfactant, or CAPSTONE® FS-63 fluorosurfactant.
9 . The film comprising the coating according to claim 1 and a transparent substrate, wherein the coating is disposed on the transparent substrate.
10 . The film according to claim 9 comprising a visible light transmittance greater than about 86 percent.