Composition for forming a contact lens
View Patent ↗There is described a composition for forming an contact lens, in particular for forming a silicone hydrogel contact lens, comprising at least one first vinylic monomer or macromer having one first ethylenically unsaturated group and at least one second vinylic monomer or macromer having one second ethylenically unsaturated group, wherein the first and second ethylenically unsaturated groups are different from each other and wherein the composition further comprises a crosslinker with at least two ethylenically unsaturated (polymerizable) groups with a selected kinetic copolymerization parameter r 1 of less than 1.0 relative to one of the first and second ethylenically unsaturated (polymerizable) groups as defined above.
1. A process for manufacturing a contact lens, comprising the steps of:
(1) providing a mold assembly comprising at least a first and a second mold half, wherein the mold assembly further comprises a mask providing for a spatial limitation of the actinic radiation defining the edge of the contact lens;
(2) dosing a lens forming material into the first mold half, wherein the lens forming material comprises
(a) from about 5% to about 60% by weight of a hydrophilic amide-type vinylic monomer,
(b) from about 5% to about 50% by weight of a siloxane-containing acrylamide vinylic monomer,
(c) from about 5% to about 50% by weight of a polysiloxane-containing vinylic monomer or macromere comprising at least one methacrylate group, and
(d) from 0.05% to 4% by weight of methylene bisacrylamide;
(3) closing the first and second mold halves to form a mold cavity defining at least the first and second surfaces of a contact lens;
(4) curing, under a spatial limitation of the actinic radiation, the lens forming material in the mold cavity; and
(5) opening the first and a second mold halves; and removing the contact lens from the first or second mold half.
2. The process of claim 1 , wherein the hydrophilic amide-type vinylic monomer is N,N-dimethylacrylamide.
3. The process of claim 2 , wherein the siloxane-containing acrylamide vinylic monomer is N-[tris(trimethylsiloxy)-silylpropyl]acrylamide.
4. The process of claim 3 , wherein the polysiloxane-containing vinylic monomer or macromere is a polydimethylsiloxane vinylic monomer or macromer.
5. The process of claim 2 , wherein the polysiloxane-containing vinylic monomer or macromere is a polydimethylsiloxane vinylic monomer or macromer.
6. The process of claim 1 , wherein the siloxane-containing acrylamide vinylic monomer is N-[tris(trimethylsiloxy)-silylpropyl]acrylamide.
7. The process of claim 6 , wherein the polysiloxane-containing vinylic monomer or macromere is a polydimethylsiloxane vinylic monomer or macromer.
8. The process of claim 1 , wherein the polysiloxane-containing vinylic monomer or macromere is a polydimethylsiloxane vinylic monomer or macromer.