Steel tube for airbags and a process for manufacturing same
View Patent ↗A steel tube for an airbag which has a low alloy cost and a strength of at least 1000 MPa and vTrs100 of −80° C. or below and a process for its manufacture which can minimize the number of times that softening annealing treatment is performed in a cold drawing step are provided. Stable properties are obtained even when quench hardening is carried out by high frequency induction heating on a large scale. The steel tube has a steel composition which comprises, in mass percent, C: 0.05-0.20%, Si: 0.10-0.50%, Mn: 0.10-1.00%, P: at most 0.025%, S: at most 0.005%, Al: 0.005-0.10%, Ca: 0.0005-0.0050%, Nb: 0.005-0.050%, Ti: 0.005-0.050%, Cu: 0.01-0.50%, Ni: 0.01-0.50%, Cr: 0.01-0.50%, B: 0.0005-0.0050%, N: 0.002-0.010%, and a remainder of Fe and unavoidable impurities.
1. A seamless steel tube for an airbag characterized by having a quenched-and-tempered microstructure and a steel composition which consists of, in mass percent,
C: 0.05-0.20%,
Si: 0.10-0.50%,
Mn: 0.10-1.00%,
P: at most 0.025%,
S: at most 0.005%,
Al: 0.005-0.10%,
Ca: 0.0005-0.0050%,
Nb: 0.005-0.050%,
Ti: 0.005-0.050%,
Cu: 0.01-0.50%,
Ni: 0.01-0.50%,
Cr: 0.01-0.50%,
B: 0.0005-0.0050%,
N: 0.002-0.010%,
and a remainder of Fe and unavoidable impurities,
and which satisfies the following Equation (1),
the tube having a tensile strength of at least 1000 MPa, a yield strength of at least 960 MPa, and a high toughness such that vTrs100 is −100° C. or below:
Cu+Ni≧(M) 2 +0.3 (1)
wherein M indicates Cr, and the symbols for elements indicate the contents in mass percent of those elements.
2. A steel tube for an airbag as set forth in claim 1 characterized in that the Ti content in mass percent is greater than 0.020% and at most 0.050%.
3. A seamless steel tube for an airbag characterized by having a quenched-and-tempered microstructure and a steel composition which consists of, in mass percent,
C: 0.05-0.20%,
Si: 0.10-0.50%,
Mn: 0.10-1.00%,
P: at most 0.025%,
S: at most 0.005%,
Al: 0.005-0.10%,
Ca: 0.0005-0.0050%,
Nb: 0.005-0.050%,
Ti: 0.005-0.050%,
Cu: 0.01-0.50%,
Ni: 0.01-0.50%,
Cr: 0.01-0.50%,
B: 0.0005-0.0050%,
N: 0.002-0.010%,
wherein the steel composition further consists of Mo: at most 0.01%;
and a remainder of Fe and unavoidable impurities,
and which satisfies the following Equation (1),
the tube having a tensile strength of at least 1000 MPa, a yield strength of at least 960 MPa, and a high toughness such that vTrs100 is −100° C. or below:
Cu+Ni≧(M) 2 +0.3 (1)
wherein M indicates (Cr+Mo), and the symbols for elements indicate the contents in mass percent of those elements.
4. A seamless steel tube for an airbag characterized by having a quenched-and-tempered microstructure and a steel composition which consists of, in mass percent,
C: 0.05-0.20%,
Si: 0.10-0.50%,
Mn: 0.10-1.00%,
P: at most 0.025%,
S: at most 0.005%,
Al: 0.005-0.10%,
Ca: 0.0005-0.0050%,
Nb: 0.005-0.050%,
Ti: 0.005-0.050%,
Cu: 0.01-0.50%,
Ni: 0.01-0.50%,
Cr: 0.01-0.50%,
B: 0.0005-0.0050%,
N: 0.002-0.010%,
V: 0.02-0.20%,
and a remainder of Fe and unavoidable impurities,
and which satisfies the following Equation (1),
the tube having a tensile strength of at least 1000 MPa, a yield strength of at least 960 MPa, and a high toughness such that vTrs100 is −100° C. or below:
Cu+Ni≧(M) 2 +0.3 (1)
wherein M indicates Cr, and the symbols for elements indicate the contents in mass percent of those elements.
5. A seamless steel tube for an airbag characterized by having a quenched-and-tempered microstructure and a steel composition which consists of, in mass percent,
C: 0.05-0.20%,
Si: 0.10-0.50%,
Mn: 0.10-1.00%,
P: at most 0.025%,
S: at most 0.005%,
Al: 0.005-0.10%,
Ca: 0.0005-0.0050%,
Nb: 0.005-0.050%,
Ti: 0.005-0.050%,
Cu: 0.01-0.50%,
Ni: 0.01-0.50%,
Cr: 0.01-0.50%,
B: 0.0005-0.0050%,
N: 0.002-0.010%,
V: 0.02-0.20%,
wherein the steel composition further consists of Mo: at most 0.01%,
and a remainder of Fe and unavoidable impurities,
and which satisfies the following Equation (1),
the tube having a tensile strength of at least 1000 MPa, a yield strength of at least 960 MPa, and a high toughness such that vTrs100 is −100° C. or below:
Cu+Ni≧(M) 2 +0.3 (1)
wherein M indicates (Cr+Mo), and the symbols for elements indicate the contents in mass percent of those elements.
6. A process for manufacturing a seamless steel tube for an airbag characterized in that a seamless steel tube manufactured by hot tube forming of a billet having a steel composition as set forth in claim 1 is subjected to cold working with a working ratio of at least 40% for one step of cold working to form a steel tube having prescribed dimensions, and the steel tube is then straightened, then subjected to quench hardening by heating to at least the Ac 3 transformation point by high frequency induction heating followed by rapid cooling, and then subjected to tempering by heating to a temperature of at most the Ac 1 transformation point.