Durable optical fiber ribbons and methods of making optical fiber ribbons
View Patent ↗Durable optical fiber ribbons are formed by promoting a strong bond between fiber ink layers and ribbon matrix material. During curing of the ink layer desired oxygen levels are maintained in the curing environment of the manufacturing process.
1. A method of forming an optical fiber ribbon, comprising:
providing optical fibers;
applying a colored ink layer to each of the optical fibers;
curing the colored ink layer in a curing environment having an Oxygen (O 2 ) content in an amount of between 10,000-100,000 parts per million (ppm) to form cured colored optical fibers;
applying a ribbon matrix material over the cured colored optical fibers; and
curing the ribbon matrix material to form a ribbon matrix in which the optical fibers are embedded,
wherein the ribbon is a no peel ribbon.
2. The method of claim 1 , wherein curing the ribbon matrix material comprises irradiating the matrix material with ultraviolet radiation.
3. The method of claim 1 , wherein providing optical fibers comprises providing coated optical fibers.
4. The method of claim 1 , wherein curing the colored ink layer comprises monitoring the Oxygen content.
5. The method of claim 1 , wherein the ribbon matrix comprises an inner and an outer matrix.
6. The method of claim 1 , wherein the optical fibers are aligned in parallel.
7. The method of claim 1 , wherein the colored ink layer is applied at a thickness in the range of 1-10 microns.
8. The method of claim 1 , wherein the ribbon matrix has a thickness of 250-330 microns at its midpoint.
9. The method of claim 1 , wherein the O 2 content is present in the curing environment in an amount of from 30,000 to 70,000 ppm.
10. The method of claim 1 , wherein presence of levels of oxygen of between 10,000-100,000 ppm in the step of curing the ink layers inhibits curing on the surface of the ink layers.
11. The method of claim 10 , wherein, prior to the step of applying the ribbon matrix, there are cure-inhibited sites on the ink layers that then continue chain propagation when the matrix material is placed in contact with the ink layer during the step of applying the ribbon matrix.
12. The method of claim 11 , wherein, during the step of curing of the matrix material, the ink layers undergo cross-linking to create bonds between the ink layers and the ribbon matrix.