Super-hydrophobic hierarchical structures, method of forming them and medical devices incorporating them
View Patent ↗Synthetic polymer substrates comprising a hierarchical surface structure of multiple domes and multiple pillars on said domes, wherein said substrate is a synthetic polymer film, said domes have diameters in the range from about 5 μm to about 400 μm, heights in the range from about 2.5 μm and about 500 μm, and said pillars have diameters in the range from about 20 nm to about 5 μm and aspect ratios of from about 2 to about 50, and methods of making and using them.
1. A method of making a synthetic polymer substrate comprising a hierarchical surface structure of multiple domes and multiple pillars on said domes, comprising:
forming an array of dome-shaped depressions, each having a diameter and a depth, in a non-aluminum solid template substrate;
forming a porous surface on said dome-shaped depressions, wherein said porous surface is formed of a material different from that of said solid template substrate; and
contacting said porous surface with a synthetic polymer thermoplastic film under temperature and pressure conditions sufficient to cause said thermoplastic to flow into pores of said porous surface and said dome-shaped depressions to form an imprinted film having said hierarchical surface structure.
2. The method of claim 1 , wherein said solid template substrate is a silicon wafer and said dome-shaped depressions are formed by lithography and dry etching.
3. The method of claim 2 , wherein said porous surface is porous anodic alumina, formed by depositing an aluminum film on said dome-shaped depressions and anodizing the aluminum film.
4. The method of claim 1 , wherein said dome-shaped depressions have diameters in the range from about 5 μm to about 400 μm, depths in the range from about 2.5 μm and about 500 μm, and pores created in said porous surface have diameters in the range from about 20 nm to about 5 μm and aspect ratios of from about 2 to about 50.
5. The method of claim 2 , wherein said dome-shaped depressions have diameters in the range from about 10 μm to about 40 μm, depths in the range from about 5 μm to about 20 μm, and the pores have diameters in the range from about 20 nm to about 500 nm and aspect ratios of from about 2 to about 50.
6. The method of claim 5 , wherein said pores have an average pore diameter of about 200 nm and an average depth of about 500 nm.
7. The method of claim 1 , wherein said synthetic polymer of said thermoplastic film is selected from the group consisting of polypropylene, polycarbonate and polydioxanone, and the thickness of said film exceeds the depth of said dome-shaped depressions.
8. The method of claim 1 , further comprising de-molding said imprinted film from said solid template substrate.
9. The method of claim 1 , wherein said solid template substrate is a metal substrate and said dome-shaped depressions are formed by micromachining.
10. The method of claim 9 , wherein said porous surface is a free standing track etched membrane having pores therein, which is placed on the surface of said solid template substrate and forced into said dome-shaped depressions under said temperature and pressure conditions.
11. The method of claim 10 , wherein said dome-shaped depressions have diameters in the range from about 50 μm to about 400 μm, depths in the range from about 50 μm and about 100 pm, and said pores have diameters in the range from about 200 nm to about 3 μm and aspect ratios of from about 2 to 50.
12. The method of claim 11 , wherein said pores have diameters in the range from about 0.4 μm to about 3 μm.
13. The method of claim 10 , further comprising placing said synthetic polymer thermoplastic film onto said track etched membrane, and applying said temperature and pressure conditions to said synthetic polymer thermoplastic film so as to force thermoplastic polymer from a surface of said film into the pores of said free standing track etched membrane and into the dome shaped depressions in said metal substrate.
14. The method of claim 10 , wherein said free standing track etched membrane is a polycarbonate filter membrane.
15. The method of claim 10 , wherein said free standing track etched membrane is a polycarbonate filter membrane, further comprising removing a combined polycarbonate filter membrane and polymer film from said mold and dissolving said polycarbonate filter membrane with a solvent, leaving said polymer substrate comprising a hierarchical surface structure.
16. A method of making a synthetic polymer substrate comprising a hierarchical surface structure of multiple domes and multiple pillars on said domes, comprising:
forming an array of dome-shaped depressions by micromachining, each having a diameter and a depth, in a metal substrate;
forming a porous surface on said dome-shaped depressions, wherein said porous surface is a free standing polycarbonate filter membrane having pores therein, which is placed on the surface of said solid template substrate and forced into said dome-shaped depressions under said temperature and pressure conditions;
contacting said porous surface with a synthetic polymer thermoplastic film under temperature and pressure conditions sufficient to cause said thermoplastic to flow into pores of said porous surface and said dome-shaped depressions to form an imprinted film having said hierarchical surface structure; and
removing a combined polycarbonate filter membrane and polymer film from said mold and dissolving said polycarbonate filter membrane with a solvent, leaving said polymer substrate comprising a hierarchical surface structure.