Methods of changing the visible light transmittance of coated articles and coated articles made thereby
A method is provided for changing the visible light transmittance of a coated article having a functional coating having at least one anti-reflective material and at least one infrared reflective material. The anti-reflective material includes an alloying material capable of combining or alloying with the infrared reflective material. A protective coating is deposited over the functional coating to prevent or retard the diffusion of atmospheric gas and/or vapor into the functional coating. The coated article is heated to a temperature sufficient to cause at least some of the alloying material to combine with at least some of the infrared reflective material to form a substance having a different visible light transmittance than the infrared reflective material.
1. A laminated article, comprising:
a first ply having a first major surface;
a functional coating over at least a portion of the first major surface and having an emissivity value;
a protective coating comprising 35 wt. % to 100 wt. % alumina and 0 wt. % to 65 wt. % silica over at least a portion of the functional coating to form a coating stack having an emissivity, the protective coating configured to increase the emissivity of the coating stack over the emissivity of the functional coating alone;
a second ply; and
an interlayer located between the first and second plies, with the protective coating facing the interlayer.
2. The article of claim 1 , wherein the first and second plies are selected from glass, plastic, and ceramic material.
3. The article of claim 1 , wherein the protective coating has a refractive index in the range of 1.5 to 2.0.
4. The article of claim 1 , wherein the protective coating increases the emissivity of the coating stack to be in the range of 0.3 to 0.9.
5. An article, comprising:
a substrate;
a functional coating over at least a portion of the substrate; and
a protective coating comprising 35 wt. % to 100 wt. % alumina and 0 wt. % to 65 wt. % silica over the functional coating, wherein the functional coating and the protective coating define a coating stack and the protective coating provides the coating stack with an emissivity higher than the emissivity of the functional coating alone.
6. The article as claimed in claim 5 , wherein the substrate is selected from glass, plastic, and ceramic.
7. The article as claimed in claim 5 , wherein the article is an automotive transparency.
8. The article as claimed in claim 5 , wherein the substrate has a thickness of 2 mm to 20 mm.
9. The article of in claim 5 , wherein the functional coating has an emissivity of 0.1 or less.
10. The article of claim 5 , wherein the protective coating increases the emissivity of the coating stack by at least a factor of two with respect to the emissivity of the functional coating.
11. The article of claim 5 , wherein the protective coating increases the emissivity of the coating stack by a factor in the range of 2 to 20 compared to the emissivity of the functional coating.
12. The article as claimed in claim 5 , wherein the functional coating has an emissivity of 0.1 or less and the coating stack has an emissivity of 0.5 or more.
13. The article as claimed in claim 5 , wherein the emissivity of the coating stack is 0.5 to 0.8.
14. The article as claimed in claim 5 , wherein the protective coating has a thickness of greater than 1 micron.
15. The article as claimed in claim 5 , wherein the protective coating has a thickness of less than 5 microns.
16. The article as claimed in claim 5 , wherein the protective coating comprises 86 wt. % to 90 wt. % alumina and 10 wt. % to 14 wt. % silica.
17. The article as claimed in claim 5 , wherein the protective coating is solar absorbing in at least one of the UV, IR, or visible regions of the electromagnetic spectrum.
18. A monolithic automotive transparency, comprising:
a glass substrate;
a functional coating over at least a portion of the glass substrate; and
a protective coating over the functional coating to form a coating stack, the protective coating comprising 35 wt. % to 100 wt. % alumina and 0 wt. % to 65 wt. % silica having a thickness in the range of 1 micron to 5 microns and providing the coating stack with an emissivity of at least 0.5.
19. The transparency as claimed in claim 18 , wherein the protective coating comprises 70 wt. % to 90 wt. % alumina and 10 wt. % to 30 wt. % silica.
20. An article, comprising:
a substrate;
a functional coating over at least a portion of the substrate; and
a protective coating comprising 10 wt. % to 90 wt. % alumina and 90 wt. % to 10 wt. % silica over the functional coating, wherein the functional coating and the protective coating define a coating stack and the protective coating provides the coating stack with an emissivity higher than the emissivity of the functional coating alone.