US 8,328,968 · App. 13/447,898 · Granted Dec 11, 2012

Abstract

Claims (10)

1. A method of preparing a composite sheet material having strength and barrier properties suitable for use as a housewrap, the method comprising:

extrusion coating a polyolefin film layer onto a surface of an area-bonded, spunbond nonwoven substrate to form a composite sheet material, the composite sheet material having a grab tensile strength of at least 178 Newtons in at least one of the machine direction (MD) or the cross-machine direction (CD), and

incrementally stretching the composite sheet material, wherein the stretching step comprises incrementally stretching the composite sheet material in at least one of the CD or the MD to form incrementally stretched zones separated by zones of substantially unstretched or less stretched material to impart to the composite sheet material a hydrostatic head of at least 100 cm, and a moisture vapor transmission rate (MVTR) of at least 35 g/m2/24 hr. at 50% relative humidity and 23° C.

2. The method according to claim 1 , comprising passing the composite sheet material through a first pair of intermeshing rolls configured for achieving stretching in the cross-direction (CD) of the composite sheet material.

3. The method according to claim 1 , comprising passing the composite sheet material through a second pair of intermeshing rolls configured for stretching in the machine direction (MD) of the composite sheet material.

4. The method according to claim 1 , wherein the nonwoven substrate has basis weight of at least 50 g/m 2 and the composite sheet material has a grab tensile strength in both the machine direction (MD) and cross-machine direction (CD) of at least 178 Newtons.

5. The method according to claim 1 , wherein the nonwoven substrate is formed from substantially continuous cold-drawn, molecularly oriented filaments.

6. The method according to claim 1 , wherein the composite sheet material has a Gurley porosity of at least 400 seconds and a basis weight of from 60 to 140 g/m 2 .

7. The method according to claim 1 , wherein the polyolefin film layer extends uninterruptedly and continuously over the surface of the nonwoven substrate and is intimately bonded thereto to provide a peel adhesion of at least 150 grams per inch, the film layer comprising a polyolefin polymer and at least 40% by weight inorganic filler, the film layer having a basis weight of at least 25 g/m 2 , and the film layer defining an outer surface of the composite sheet material.

8. The method according to claim 1 , wherein the stretching step comprises stretching the composite sheet material in both the CD and the MD by incremental stretching to impart to the composite sheet material a moisture vapor transmission rate (MVTR) of at least 100 g/m 2 /24 hr at 50% relative humidity and 23° C.

Assignments (45)