Treatment of fly ash for use in concrete
View Patent ↗A process for treating fly ash to render it highly usable as a concrete additive. A quantity of fly ash is obtained that contains carbon and which is considered unusable fly ash for concrete based upon foam index testing. The fly ash is mixed with an activator solution sufficient to initiate a geopolymerization reaction and for a geopolymerized fly ash. The geopolymerized fly ash is granulated. The geopolymerized fly ash is considered usable fly ash for concrete according to foam index testing. The geopolymerized fly ash may have a foam index less than 35% of the foam index of the untreated fly ash, and in some cases less than 10% of the foam index of the untreated fly ash. The activator solution may contain an alkali metal hydroxide, carbonate, silicate, aluminate, or mixtures thereof.
1. A geopolymerized fly ash generated by a method comprising the steps of:
obtaining a quantity of fly ash that contains carbon and has a foam index;
mixing the fly ash with an activator solution sufficient to initiate a geopolymerization reaction and form a geopolymerized fly ash; and
granulating the geopolymerized fly ash, wherein the geopolymerized fly ash is considered, at a minimum, usable fly ash for concrete according to foam index testing.
2. The geopolymerized fly ash of claim 1 , wherein the activator solution comprises an activator selected from the group consisting of a metal carbonate, a metal silicate, a metal aluminate, a metal sulfate, a metal hydroxide, and mixtures thereof.
3. The geopolymerized fly ash of claim 1 , wherein the activator solution comprises a metal carbonate.
4. The geopolymerized fly ash of claim 1 , wherein the activator solution comprises a metal hydroxide.
5. The geopolymerized fly ash of claim 1 , wherein the ratio of activator to fly ash is between 1:50 and 10:1.
6. The geopolymerized fly ash of claim 1 , wherein the geopolymerized fly ash is granulated by spray drying.
7. The geopolymerized fly ash of claim 1 , wherein the geopolymerized fly ash is heated to a temperature between 20 and 250° C.
8. The geopolymerized fly ash of claim 1 , wherein the geopolymerized fly ash is granulated by crushing.
9. The geopolymerized fly ash of claim 1 , wherein the granulated, geopolymerized fly ash has a mean particle size between 0.1 and 1000 microns.
10. The geopolymerized fly ash of claim 1 , wherein the granulated, geopolymerized fly ash has a mean particle size between 10 and 100 microns.
11. The geopolymerized fly ash of claim 1 , wherein the geopolymerized fly ash is considered premium grade for concrete based upon foam index testing.
12. The geopolymerized fly ash of claim 1 , wherein the geopolymerized fly ash is considered standard grade for concrete based upon foam index testing.
13. The geopolymerized fly ash of claim 1 , wherein the fly ash contains one or more heavy metals.
14. The geopolymerized fly ash of claim 1 , further comprising the step of mixing the granulated and geopolymerized fly ash with an activator solution sufficient to initiate a second geopolymerization reaction and form a second geopolymerized fly ash.
15. The geopolymerized fly ash of claim 1 , wherein the geopolymerized fly ash has foam index less than 35% of the foam index of the untreated fly ash.
16. A geopolymerized fly ash generated by a method comprising the steps of:
obtaining a quantity of fly ash that contains carbon and has a foam index;
mixing the fly ash with an activator solution sufficient to initiate a geopolymerization reaction and form a geopolymerized fly ash, wherein the ratio of activator to fly ash is between 1:50 and 10:1;
heating the geopolymerized fly ash to a temperature between 20 and 250° C.; and
granulating the geopolymerized fly ash, wherein the geopolymerized fly ash has foam index less than 35% of the foam index of the untreated fly ash, and wherein the granulated, geopolymerized fly ash has a mean particle size between 0.1 and 1000 microns.
17. The process according to claim 16 , wherein the geopolymerized fly ash has a foam index less than 20% of the foam index of the untreated fly ash.
18. The process according to claim 16 , wherein the geopolymerized fly ash has a foam index less than 10% of the foam index of the untreated fly ash.
19. The process according to claim 16 , further comprising the step of mixing the granulated and geopolymerized fly ash with an activator solution sufficient to initiate a second geopolymerization reaction and form a second geopolymerized fly ash.