Fiber cement building materials with low density additives
View Patent ↗This invention relates to a formulation with the addition of low density additives of volcanic ash, hollow ceramic microspheres or a combination of microspheres and volcanic ash or other low density additives into cementitious cellulose fiber reinforced building materials. This formulation is advantageously lightweight or low density compared as compared to current fiber cement products without the increased moisture expansion and freeze-thaw degradation usually associated with the addition of lightweight inorganic materials to fiber cement mixes. The low density additives also give the material improved thermal dimensional stability.
1. A Hatschek manufactured board, comprising:
about 5%-80% of Portland cement;
about 0%-80% silica;
a plurality of hollow microspheres, said hollow microspheres having a median particle size between 20 to 120 micrometers, wherein the hollow microspheres are dispersed in the Hatschek manufactured board to introduce pores in the board, said hollow microspheres comprising about 62%-65% silica, about 23%-26% alumina, and about 3%-4% iron oxide; and
wherein the hollow microspheres lower the density of the Hatschek manufactured board to less than 1.2 g/cm 3 .
2. The Hatschek manufactured board of claim 1 , wherein the density of the Hatschek manufactured board is about 0.9 to 1.1 g/cm 3 .
3. The Hatschek manufactured board of claim 1 , wherein the median particle size of the microspheres is between about 80 and 120 micrometers.
4. The Hatschek manufactured board of claim 1 , wherein hollow microspheres comprises about 2% to 90 wt. % of the Hatschek manufactured board.
5. The Hatschek manufactured board of claim 1 further comprising about 0%-30% calcium silicate hydrate.