Hot-rolled steel bar or wire rod
View Patent ↗A hot-rolled steel bar or wire rod consisting of C: 0.1 to 0.3%, Si: 0.05 to 1.5%, Mn: 0.4 to 2.0%, S: 0.003 to 0.05%, Cr: 0.5 to 3.0%, Al: 0.02 to 0.05%, and N: 0.010 to 0.025%, the balance being Fe and impurities, and the impurities containing P: 0.025% or less, Ti: 0.003% or less, and O: 0.002% or less, wherein the structure thereof is composed of a ferrite-pearlite structure, ferrite-pearlite-bainite structure, or ferrite-bainite structure; the standard deviation of ferrite fractions at the time when randomly selected 15 viewing fields of a transverse cross section are observed and measured with the area per one viewing field being 62,500 μm 2 is 0.10 or less; and in a region from the surface to one-fifth of the radius and a region from the center to one-fifth of the radius in the transverse cross section, the amount of Al precipitating as AlN is 0.005% or less, and the density in terms of the number of AlN having a diameter of 100 nm or larger is 5/100 μm 2 or less. In the hot-rolled steel bar or wire rod, even if hot forging is performed in various temperature ranges, austenite grains can be stably prevented from being coarsened at the time of heating for carburization.
1. A hot-rolled steel bar or wire rod having a chemical composition consisting of, by mass percent, C: 0.1 to 0.3%, Si: 0.05 to 1.5%, Mn: 0.4 to 2.0%, S: 0.003 to 0.05%, Cr: 0.5 to 3.0%, Al: 0.02 to 0.05%, and N: 0.010 to 0.025%, the balance being Fe and impurities, and the contents of P, Ti and O in the impurities being P: 0.025% or less, Ti: 0.003% or less, and O: 0.002% or less, wherein
the structure of the hot-rolled steel bar or wire rod is composed of a ferrite-pearlite structure, ferrite-pearlite-bainite structure, or ferrite-bainite structure;
the standard deviation of ferrite fractions at the time when randomly selected 15 viewing fields of a transverse cross section are observed and measured with the area per one viewing field being 62,500 μm 2 is 0.10 or less; and
when a region from the surface to one-fifth of the radius and a region from the center to one-fifth of the radius in the transverse cross section are observed, in each of the regions, the amount of Al precipitating as AlN is 0.005% or less, and the density in terms of the number of AlN having a diameter of 100 nm or larger is 5/100 μm 2 or less.
2. The hot-rolled steel bar or wire rod according to claim 1 , wherein the chemical composition further contains, by mass percent, at least one element selected from Ni: 1.5% or less and Mo: 0.8% or less in lieu of part of Fe.
3. The hot-rolled steel bar or wire rod according to claim 1 , wherein the chemical composition further contains, by mass percent, at least one element selected from Nb: 0.08% or less and V: 0.2% or less in lieu of part of Fe.
4. The hot-rolled steel bar or wire rod according to claim 2 , wherein the chemical composition further contains, by mass percent, at least one element selected from Nb: 0.08% or less and V: 0.2% or less in lieu of part of Fe.