Superabsorbent polymers and methods of making the same

1. A process for producing a superabsorbent polymer comprising the steps of:

I a) producing crude (meth)acrylic acid phase wherein crude (meth)acrylic acid comprises from about 1 to about 80 wt % of (meth)acrylic acid; wherein said producing crude (meth)acrylic acid phase is selected from the group consisting of gas phase oxidation, dehydration of an organic molecule having at least one OH-group wherein the organic molecule is selected from the group consisting of glycerine, lactic acid and β-hydroxypropionic acid, optionally followed by an oxidation, and liquid phase oxidation;

b) distilling the (meth)acrylic acid phase of a) to obtain a (meth)acrylic acid phase, and a dimer base comprising (meth)acrylic acid dimers or (meth)acrylic acid oligomers or both;

c) splitting at least a part of the (meth)acrylic acid dimers or of the (meth)acrylic acid oligomers or both from the dimer phase to obtain a (meth)acrylic acid-comprising low boiling phase, and a high boiling phase comprising less (meth)acrylic acid than the low boiling phase, wherein said high boiling phase is discarded;

d) separating at least a part of the (meth)acrylic acid from the low boiling phase by forming one or more crystals to obtain a pure (meth)acrylic acid and a residue;

II. polymerizing the (meth)acrylic acid in the presence of a cross linker to obtain a superabsorber polymer phase; and

III. working-up the polymer phase to obtain the superabsorbent polymer.

2. The process according to claim 1 , wherein at least a part of the low boiler phase in step d) is provided as fluid film over a cold source.

3. The process according to claim 2 , wherein at least a part of the fluid film comprises a falling film.

4. The process according to claim 2 , wherein the cold source comprises an at least partially planar form.

5. The process according to claim 1 , wherein at least a part of the crystals are subjected to a sweating.

6. The process according to claim 5 , wherein the crystals are melted after the sweating.

7. The process according to claim 1 , wherein the distillative work-up according to step b) occurs in at least two distillation steps following each other.

8. The process according to claim 1 , wherein the splitting according to step c) occurs thermally.

9. The process according to claim 8 , wherein the splitting according to step c) occurs under a pressure which is different from the ambient pressure.

10. The process according to claim 1 , further comprising the step of e) crystallizing the residue of step d) into a (meth)acrylic acid-rich phase, and an impurity phase.

11. The process according to claim 10 wherein the (meth)acrylic acid-rich phase is at least partially supplied to process step d).