View Patent ↗The present invention provides a duplex stainless steel having excellent resistance to alkalis and particularly corrosion resistance against high-temperature concentrated alkali solutions and excellent weldability. The duplex stainless steel has a chemical composition comprising, in mass %, C: at most 0.03%, Si: at most 0.5%, Mn: at most 2.0%, P: at most 0.04%, S: at most 0.003%, Cr: at least 25.0% to less than 28.0%, Ni: at least 6.0% to at most 10.0%, Mo: at least 0.2% to at most 3.5%, N: less than 0.5%, W: at most 3.0%, and a remainder of Fe and impurities.
1. A duplex stainless steel for use in applications requiring alkali resistance having a chemical composition comprising, in mass %, C: at most 0.03%, Si: at most 0.5%, Mn: at most 2.0%, P: at most 0.04%, S: at most 0.003%, Cr: at least 25.0% to less than 28.0%, Ni: at least 6.0% to at most 10.0%, Mo: at least 0.2% to at most 3.5%, N: less than 0.5%, W: at most 3.0%, and a remainder of Fe and impurities, wherein the duplex stainless steel is rolled and it has an average transverse grain diameter of austenite grains in a rolling stretcher section of at most 350 μm.
2. A duplex stainless steel as set forth in claim 1 characterized in that the ferrite content of the duplex stainless steel is at least 40 mass %.
3. A duplex stainless steel as set forth in claim 1 characterized in that the number of ferrite phases present in a region between the surface of the duplex stainless steel and a depth of 0.5 mm from the surface is at least 15.
4. A duplex stainless steel as set forth in claim 2 characterized in that the number of ferrite phases present in a region between the surface of the duplex stainless steel and a depth of 0.5 mm from the surface is at least 15.
5. The duplex stainless steel as set forth in claim 1 , wherein a content of Mo+W is 1.0 to 5.0%.
6. A duplex stainless steel for use in applications requiring alkali resistance having a chemical composition consisting essentially of, in mass %, C: at most 0.03%, Si: at most 0.5%, Mn: at most 2.0%, P: at most 0.04%, S: at most 0.003%, Cr: at least 25.0% to less than 28.0%, Ni: at least 6.0% to at most 10.0%, Mo: at least 0.2% to at most 3.5%, N: less than 0.5%, W: at most 3.0%, and a remainder of Fe and impurities, wherein the duplex stainless steel is rolled and it has an average transverse grain diameter of austenite grains in a rolling stretcher section of at most 350 μm.
7. A duplex stainless steel as set forth in claim 6 characterized in that the ferrite content of the duplex stainless steel is at least 40 mass %.
8. A duplex stainless steel as set forth in claim 6 characterized in that the number of ferrite phases present in a region between the surface of the duplex stainless steel and a depth of 0.5 mm from the surface is at least 15.
9. A duplex stainless steel as set forth in claim 7 characterized in that the number of ferrite phases present in a region between the surface of the duplex stainless steel and a depth of 0.5 mm from the surface is at least 15.
10. The duplex stainless steel as set forth in claim 6 , wherein a content of Mo+W is 1.0 to 5.0%.